高级搜索

电子束辐照剂量对PAN/PEO交联度的影响

,  ,  ,  ,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

马艺准, 张崇宏, 张子民, 肖荣庆, 宋银, 杨义涛, 张丽卿, 孟彦成, 张恒庆, 缑洁. 2014: 电子束辐照剂量对PAN/PEO交联度的影响, 原子核物理评论, null(1): 86-91. doi: 10.11804/NuclPhysRev.31.01.086
引用本文: 马艺准, 张崇宏, 张子民, 肖荣庆, 宋银, 杨义涛, 张丽卿, 孟彦成, 张恒庆, 缑洁. 2014: 电子束辐照剂量对PAN/PEO交联度的影响, 原子核物理评论, null(1): 86-91. doi: 10.11804/NuclPhysRev.31.01.086
shu
MA Yizhun, ZHANG Chonghong, ZHANG Zimin, XIAO Rongqing, SONG Yin, YANG Yitao, ZHANG Liqing, MENG Yancheng, ZHANG Hengqing, GOU Jie. 2014: Electron Beam Irradiation Dose Effects on Crosslinking Degree of PAN/PEO, Nuclear Physics Review, null(1): 86-91. doi: 10.11804/NuclPhysRev.31.01.086
Citation: MA Yizhun, ZHANG Chonghong, ZHANG Zimin, XIAO Rongqing, SONG Yin, YANG Yitao, ZHANG Liqing, MENG Yancheng, ZHANG Hengqing, GOU Jie. 2014: Electron Beam Irradiation Dose Effects on Crosslinking Degree of PAN/PEO, Nuclear Physics Review, null(1): 86-91. doi: 10.11804/NuclPhysRev.31.01.086
shu

电子束辐照剂量对PAN/PEO交联度的影响

  • 中国科学院近代物理研究所,兰州,730000

  • 中国科学院近代物理研究所，兰州 730000; 甘肃省粒子束辐照研究中心，兰州 730000

  • 中国科学院近代物理研究所，兰州 730000; 中国科学院大学，北京 100049

Electron Beam Irradiation Dose Effects on Crosslinking Degree of PAN/PEO

  • 摘要: 对PAN/PEO凝胶(5% PAN，5% PEO)在1.0 MeV电子束下进行了不同剂量的辐照。红外光谱测量表明，PAN/PEO凝胶辐照后发生了化学交联。分析结果指出，PAN/PEO的凝胶分数随着辐照剂量的增加而不断增加；其凝胶分数增长率的变化可以分为3个阶段，即快速增加阶段(0～39 kGy)、下降阶段(39～130 kGy)和稳定阶段(>130 kGy)。拟合发现，引入材料刚性参数β的半经验修正方程与未考虑材料刚性的Charlesby-Pinner方程相比，更符合实际测量值(对于该配比PAN/PEO，β为0.166)。交联度-辐照剂量曲线显示，交联度随辐照剂量的增加而增加，为设计新型能功能材料中所需的固定交联度的PAN/PEO凝胶提供了辐照剂量参考值。
    Abstract: Polyacrylonitrile/polyethylene oxide (PAN/PEO, 5% PAN and 5% PEO) was irradiated by 1.0 MeV electron beam with different doses in this work. FTIR result indicated that PAN/PEO crosslinked after irradiation. It was pointed out by analysis that gel fraction of PAN/PEO increased with EB irradiation dose. The increasing rate of gel fraction could be divided into three stages, which were rapidly increasing stage (0～39 kGy), decreasing stage (39～130 kGy) and stable stage (more than 130 kGy). Theoretical calculation results showed that the values fitting by half-experience equation presented by Zhang Wanxi were closer to the measured values than Charlesby-Pinner equation fitting ones because of the introduction of rigidity parameterβ in the half-experience equation (for PAN/PEO,β was 0.166). The curve of crosslinking degree vs irradiation dose showed that the crosslinking degree increased with the irradiation dose, and it could provide a referential irradiation dose when materials with fixed crosslinking degree were needed in new functional materials.
  • 加载中
  • 加载中
计量
  • 文章访问数:  322
  • HTML全文浏览数:  88
  • PDF下载数:  0
  • 施引文献:  0
出版历程
  • 刊出日期:  2014-03-20

电子束辐照剂量对PAN/PEO交联度的影响

  • 中国科学院近代物理研究所,兰州,730000
  • 中国科学院近代物理研究所，兰州 730000; 甘肃省粒子束辐照研究中心，兰州 730000
  • 中国科学院近代物理研究所，兰州 730000; 中国科学院大学，北京 100049

摘要: 对PAN/PEO凝胶(5% PAN，5% PEO)在1.0 MeV电子束下进行了不同剂量的辐照。红外光谱测量表明，PAN/PEO凝胶辐照后发生了化学交联。分析结果指出，PAN/PEO的凝胶分数随着辐照剂量的增加而不断增加；其凝胶分数增长率的变化可以分为3个阶段，即快速增加阶段(0～39 kGy)、下降阶段(39～130 kGy)和稳定阶段(>130 kGy)。拟合发现，引入材料刚性参数β的半经验修正方程与未考虑材料刚性的Charlesby-Pinner方程相比，更符合实际测量值(对于该配比PAN/PEO，β为0.166)。交联度-辐照剂量曲线显示，交联度随辐照剂量的增加而增加，为设计新型能功能材料中所需的固定交联度的PAN/PEO凝胶提供了辐照剂量参考值。