高级搜索

PAMS微球制备过程中电解质的影响

,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

陈素芬, 李洁, 刘梅芳, 刘一杨, 苏琳, 张占文, 李波. 2014: PAMS微球制备过程中电解质的影响, 强激光与粒子束, 26(7): 48-53. doi: 10.11884/HPLPB201426.072001
引用本文: 陈素芬, 李洁, 刘梅芳, 刘一杨, 苏琳, 张占文, 李波. 2014: PAMS微球制备过程中电解质的影响, 强激光与粒子束, 26(7): 48-53. doi: 10.11884/HPLPB201426.072001
shu
Chen Sufen, Li Jie, Liu Meifang, Liu Yiyang, Su Lin, Zhang Zhanwen, Li Bo. 2014: Influences of electrolyte in fabrication process of poly (or-methyl styrene) capsules by microencapsulation, High Power Lase and Particle Beams, 26(7): 48-53. doi: 10.11884/HPLPB201426.072001
Citation: Chen Sufen, Li Jie, Liu Meifang, Liu Yiyang, Su Lin, Zhang Zhanwen, Li Bo. 2014: Influences of electrolyte in fabrication process of poly (or-methyl styrene) capsules by microencapsulation, High Power Lase and Particle Beams, 26(7): 48-53. doi: 10.11884/HPLPB201426.072001
shu

PAMS微球制备过程中电解质的影响

  • 中国工程物理研究院激光聚变研究中心,四川绵阳,621900

Influences of electrolyte in fabrication process of poly (or-methyl styrene) capsules by microencapsulation

  • 摘要: 为调控固化过程中双重乳液内径的变化和降低聚α甲基苯乙烯(PAMS)微球的表面粗糙度,研究了双重乳液固化过程中内外水相中电解质浓度对水在油相液膜中迁移和分相行为的影响.结果表明:仅在外水相中添加电解质时,内水相的渗透压高于外水相,使得内相水向外水相迁移,导致固化后的微球表面起皱.当在内外水相同时添加电解质时,由于平衡了三相之间水的化学势,抑制了水在油相液膜中的迁移和分相,导致PAMS微球壳壁内气泡体积和数量显著降低.同时,在内外水相中同时添加不同浓度的电解质,还可显著改善双重乳液三相之间的密度匹配度,从而提高微球的球形度和壁厚均匀性.
  • 加载中
  • 加载中
计量
  • 文章访问数:  230
  • HTML全文浏览数:  11
  • PDF下载数:  6
  • 施引文献:  0
出版历程
  • 刊出日期:  2014-07-30

PAMS微球制备过程中电解质的影响

  • 中国工程物理研究院激光聚变研究中心,四川绵阳,621900

摘要: 为调控固化过程中双重乳液内径的变化和降低聚α甲基苯乙烯(PAMS)微球的表面粗糙度,研究了双重乳液固化过程中内外水相中电解质浓度对水在油相液膜中迁移和分相行为的影响.结果表明:仅在外水相中添加电解质时,内水相的渗透压高于外水相,使得内相水向外水相迁移,导致固化后的微球表面起皱.当在内外水相同时添加电解质时,由于平衡了三相之间水的化学势,抑制了水在油相液膜中的迁移和分相,导致PAMS微球壳壁内气泡体积和数量显著降低.同时,在内外水相中同时添加不同浓度的电解质,还可显著改善双重乳液三相之间的密度匹配度,从而提高微球的球形度和壁厚均匀性.