高级搜索

ZnS与SiO2材料的短脉冲激光热损伤特性比较

,  ,  ,  , 

downloadPDF

上一篇

下一篇

朱晓冰, 付博, 杜立峰, 李风雨, 张蓉竹. 2014: ZnS与SiO2材料的短脉冲激光热损伤特性比较, 强激光与粒子束, 26(12): 20-25. doi: 10.11884/HPLPB201426.121002
引用本文: 朱晓冰, 付博, 杜立峰, 李风雨, 张蓉竹. 2014: ZnS与SiO2材料的短脉冲激光热损伤特性比较, 强激光与粒子束, 26(12): 20-25. doi: 10.11884/HPLPB201426.121002
shu
Zhu Xiaobing, Fu Bo, Du Lifeng, Li Fengyu, Zhang Rongzhu. 2014: Comparative analysis on thermal damage characteristics of ZnS and SiO2 induced by short pulse laser, High Power Lase and Particle Beams, 26(12): 20-25. doi: 10.11884/HPLPB201426.121002
Citation: Zhu Xiaobing, Fu Bo, Du Lifeng, Li Fengyu, Zhang Rongzhu. 2014: Comparative analysis on thermal damage characteristics of ZnS and SiO2 induced by short pulse laser, High Power Lase and Particle Beams, 26(12): 20-25. doi: 10.11884/HPLPB201426.121002
shu

ZnS与SiO2材料的短脉冲激光热损伤特性比较

  • 四川大学电子信息学院,成都,610064

  • 中国工程物理研究院流体物理研究所,四川绵阳,621900

Comparative analysis on thermal damage characteristics of ZnS and SiO2 induced by short pulse laser

  • 摘要: 对SiO2和ZnS这两种常用的红外光学材料在红外短脉冲激光辐照下的热损伤特性进行了研究,分析了相同激光辐照条件下两种材料的热效应,另外也针对同种材料不同辐照条件下的热效应进行比较.分析结果表明:红外激光作用下,SiO2材料的表面温升快于ZnS材料,而在材料内部,则后者快于前者.脉冲辐照结束时SiO2材料的表面峰值温度高于ZnS材料,但ZnS材料产生温升的深度大于SiO2材料.由于能量更为集中,材料在皮秒激光作用下温升高于纳秒激光作用下的温升.若材料的峰值温度达到熔点,则激光的单脉冲能量随脉冲宽度的减小呈非线性减小趋势,且变化率越来越大.
  • 加载中
  • 加载中
计量
  • 文章访问数:  343
  • HTML全文浏览数:  147
  • PDF下载数:  22
  • 施引文献:  0
出版历程
  • 刊出日期:  2014-12-30

ZnS与SiO2材料的短脉冲激光热损伤特性比较

  • 四川大学电子信息学院,成都,610064
  • 中国工程物理研究院流体物理研究所,四川绵阳,621900

摘要: 对SiO2和ZnS这两种常用的红外光学材料在红外短脉冲激光辐照下的热损伤特性进行了研究,分析了相同激光辐照条件下两种材料的热效应,另外也针对同种材料不同辐照条件下的热效应进行比较.分析结果表明:红外激光作用下,SiO2材料的表面温升快于ZnS材料,而在材料内部,则后者快于前者.脉冲辐照结束时SiO2材料的表面峰值温度高于ZnS材料,但ZnS材料产生温升的深度大于SiO2材料.由于能量更为集中,材料在皮秒激光作用下温升高于纳秒激光作用下的温升.若材料的峰值温度达到熔点,则激光的单脉冲能量随脉冲宽度的减小呈非线性减小趋势,且变化率越来越大.