高级搜索

La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应

,  ,  ,  , 

downloadPDF

上一篇

下一篇

陈伟, 钟伟, 都有为, 潘成福, 常虹. 2001: La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应, 物理学报, 50(2): 319-323. doi: 10.3321/j.issn:1000-3290.2001.02.024
引用本文: 陈伟, 钟伟, 都有为, 潘成福, 常虹. 2001: La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应, 物理学报, 50(2): 319-323. doi: 10.3321/j.issn:1000-3290.2001.02.024
shu
CHEN WEI, ZHONG WEI, DU YOU-WEI, PAN CHENG-FU, CHANG HONG. 2001: CURIE TEMPERATURE AND MAGNETOCALORIC EFFECT OF POLYCRYSTALLINE La0.8-xCa0.2MnO3, Acta Physica Sinica, 50(2): 319-323. doi: 10.3321/j.issn:1000-3290.2001.02.024
Citation: CHEN WEI, ZHONG WEI, DU YOU-WEI, PAN CHENG-FU, CHANG HONG. 2001: CURIE TEMPERATURE AND MAGNETOCALORIC EFFECT OF POLYCRYSTALLINE La0.8-xCa0.2MnO3, Acta Physica Sinica, 50(2): 319-323. doi: 10.3321/j.issn:1000-3290.2001.02.024
shu

La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应

  • 南京大学；山东大学物理系,；河北师范大学物理系,

  • 南京大学

  • 河北师范大学物理系,

CURIE TEMPERATURE AND MAGNETOCALORIC EFFECT OF POLYCRYSTALLINE La0.8-xCa0.2MnO3

  • 摘要: 采用溶胶-凝胶法制备了系列La0.8-xCa0.2MnO3多晶样品，用X射线衍射分析确定了样品的钙钛矿结构，用透射电子显微镜观察了样品的形貌及粒径分布情况，用PAR155型振动样品磁强计测量了样品的磁性随外场和温度的变化，确定样品的居里温度并计算了各样品的磁熵变. 磁测量及计算结果表明制备的各样品的居里温度在180—260K的范围内且随焙烧温度和La3+离子空位浓度的不同而变化，不同温度焙烧的样品均有较大的磁熵变值，其中1100℃焙烧的La0.77Ca0.2MnO3，多晶样品在240.5K，H=1.0T的外场下的磁熵变达3.76J/kg·K，对实验结果做了定性的分析. 该材料具有较高的居里温度和较大的磁熵变，所需外场强度适中，电阻率高，性能稳定，适合做高温磁制冷材料.
    Abstract: Polycrystalline samples of La0.8-xCa0.2MnO3(x=0，0.01，0.03，0.05，0.08，0.1) were synthesized using a sol-gel technique. Structure analysis, morphology observation and magnetic measurement have been used to study the effect of vacuum concentration of La3+ on the Curie temperature and magnetic entropy change of La0.8-xCa0.2MnO3. The experimental results show that by tuning the vacuum concentration of La3+, the materials could exhibit very different Curie temperatures (from 180 to 260K). All the samples in this paper have large magnetic entropy change, especially for La0.77Ca0.2MnO3 sintered at 1100℃, which has a very large magnetic entropy change ΔSM=3.76J/kg·K under the magnetic field H=1.0T. The phenomenon of large magnetic entropy change, high Curie temperature, high electrical resistivity and high chemical stability make this material a suitable candidates for refrigerants at high temperature.
  • 加载中
  • 加载中
计量
  • 文章访问数:  606
  • HTML全文浏览数:  96
  • PDF下载数:  61
  • 施引文献:  0
出版历程

La0.8-xCa0.2MnO3纳米颗粒的居里温度与磁热效应

  • 南京大学；山东大学物理系,；河北师范大学物理系,
  • 南京大学
  • 河北师范大学物理系,

摘要: 采用溶胶-凝胶法制备了系列La0.8-xCa0.2MnO3多晶样品，用X射线衍射分析确定了样品的钙钛矿结构，用透射电子显微镜观察了样品的形貌及粒径分布情况，用PAR155型振动样品磁强计测量了样品的磁性随外场和温度的变化，确定样品的居里温度并计算了各样品的磁熵变. 磁测量及计算结果表明制备的各样品的居里温度在180—260K的范围内且随焙烧温度和La3+离子空位浓度的不同而变化，不同温度焙烧的样品均有较大的磁熵变值，其中1100℃焙烧的La0.77Ca0.2MnO3，多晶样品在240.5K，H=1.0T的外场下的磁熵变达3.76J/kg·K，对实验结果做了定性的分析. 该材料具有较高的居里温度和较大的磁熵变，所需外场强度适中，电阻率高，性能稳定，适合做高温磁制冷材料.

English Abstract