高级搜索

含碳纳米颗粒凝胶玻璃的制备及其量子尺寸效应

,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

杨合情, 王喧, 刘守信, 李永放, 张良莹, 姚熹. 2001: 含碳纳米颗粒凝胶玻璃的制备及其量子尺寸效应, 物理学报, 50(2): 341-346. doi: 10.3321/j.issn:1000-3290.2001.02.028
引用本文: 杨合情, 王喧, 刘守信, 李永放, 张良莹, 姚熹. 2001: 含碳纳米颗粒凝胶玻璃的制备及其量子尺寸效应, 物理学报, 50(2): 341-346. doi: 10.3321/j.issn:1000-3290.2001.02.028
shu
YANG He-Qing, WANG XUAN, LIU Shou-xin, LI Yong-fang, ZHANG Liang-ying, YAO XI. 2001: SYNTHESIS AND QUANTUM SIZE EFFECT OF CARBON NANOPARTICLES DOPED IN GEL-GLASSES, Acta Physica Sinica, 50(2): 341-346. doi: 10.3321/j.issn:1000-3290.2001.02.028
Citation: YANG He-Qing, WANG XUAN, LIU Shou-xin, LI Yong-fang, ZHANG Liang-ying, YAO XI. 2001: SYNTHESIS AND QUANTUM SIZE EFFECT OF CARBON NANOPARTICLES DOPED IN GEL-GLASSES, Acta Physica Sinica, 50(2): 341-346. doi: 10.3321/j.issn:1000-3290.2001.02.028
shu

含碳纳米颗粒凝胶玻璃的制备及其量子尺寸效应

  • 陕西师范大学,；复旦大学

  • 陕西师范大学,

  • 西安交通大学电子材料与器件研究所,

SYNTHESIS AND QUANTUM SIZE EFFECT OF CARBON NANOPARTICLES DOPED IN GEL-GLASSES

  • 摘要: 以磷酸三乙酯、硝酸铝和正硅酸乙酯为原料，通过它们的不完全水解制备了含有有机基团的xAl2O3-xP2O5-100SiO2(x=0.25—3)凝胶.在空气中在400℃或450℃或在氮气中从300到700℃对凝胶进行热处理，使凝胶中的有机基团炭化，从而得到含有碳纳米颗粒的xAl2O3-xP2O5-100SiO2(x=0.25—2)凝胶玻璃.利用吸收光谱和TEM对含有碳纳米颗粒的凝胶玻璃进行了表征，结果发现随着碳纳米颗粒尺寸的减小吸收边向高能边移动，这种现象是由碳纳米颗粒中电子和空穴的量子限制效应引起的.电子衍射表明凝胶玻璃中的纳米碳为非晶碳.
    Abstract: C-nanoparticles with a diameter smaller than 60 nm in xAl2O3xP2O5-100SiO2(x=0.25—2) gel-glasses have been prepared by sol-gel process. The gels synthesized through partial hydrolysis of PO(OC2H5)3,Al(NO3)3·9H2O and Si(OC2H5)4 were heated at 400℃ or 450℃ in air atmosphere or from 300 to 700℃ in N2 atmosphere, in which —OC\-2H\-5 were carbonized to form nanosized C particles. These C-nanoparticles-doped gel-glasses were characterized by optical absorption and TEM.The optical absorption edge shifts to the higher-energy side as the size of the C particle decreases. This phenomenon is interpreted in terms of a quantum confinement effect of electron and hole in the C-nanoparticles. The C-nanoparticles structures were found to be amorphous carbon in the gel-glasses by electron diffraction pattern.
  • 加载中
  • 加载中
计量
  • 文章访问数:  452
  • HTML全文浏览数:  57
  • PDF下载数:  39
  • 施引文献:  0
出版历程
  • 刊出日期:  2001-02-28

含碳纳米颗粒凝胶玻璃的制备及其量子尺寸效应

  • 陕西师范大学,；复旦大学
  • 陕西师范大学,
  • 西安交通大学电子材料与器件研究所,

摘要: 以磷酸三乙酯、硝酸铝和正硅酸乙酯为原料，通过它们的不完全水解制备了含有有机基团的xAl2O3-xP2O5-100SiO2(x=0.25—3)凝胶.在空气中在400℃或450℃或在氮气中从300到700℃对凝胶进行热处理，使凝胶中的有机基团炭化，从而得到含有碳纳米颗粒的xAl2O3-xP2O5-100SiO2(x=0.25—2)凝胶玻璃.利用吸收光谱和TEM对含有碳纳米颗粒的凝胶玻璃进行了表征，结果发现随着碳纳米颗粒尺寸的减小吸收边向高能边移动，这种现象是由碳纳米颗粒中电子和空穴的量子限制效应引起的.电子衍射表明凝胶玻璃中的纳米碳为非晶碳.