高级搜索

Yb:FAP和Yb:C3S2-FAP晶体光谱的温度特性和选择激发

,  ,  , 

downloadPDF

上一篇

下一篇

毛艳丽, 赵志伟, 邓佩珍, 干福熹. 2004: Yb:FAP和Yb:C3S2-FAP晶体光谱的温度特性和选择激发, 物理学报, 53(5): 1524-1528. doi: 10.3321/j.issn:1000-3290.2004.05.047
引用本文: 毛艳丽, 赵志伟, 邓佩珍, 干福熹. 2004: Yb:FAP和Yb:C3S2-FAP晶体光谱的温度特性和选择激发, 物理学报, 53(5): 1524-1528. doi: 10.3321/j.issn:1000-3290.2004.05.047
shu
2004: Temperature and selective excitation properties of the spectra for Yb:FAP and Yb:C3S2-FAP crystals, Acta Physica Sinica, 53(5): 1524-1528. doi: 10.3321/j.issn:1000-3290.2004.05.047
Citation: 2004: Temperature and selective excitation properties of the spectra for Yb:FAP and Yb:C3S2-FAP crystals, Acta Physica Sinica, 53(5): 1524-1528. doi: 10.3321/j.issn:1000-3290.2004.05.047
shu

Yb:FAP和Yb:C3S2-FAP晶体光谱的温度特性和选择激发

  • 河南大学物理与信息光电子学院,开封,475001

  • 中国科学院上海光学精密机械研究所,上海,201800

Temperature and selective excitation properties of the spectra for Yb:FAP and Yb:C3S2-FAP crystals

  • 摘要: 报导了Yb:FAP和Yb:C3S2-FAP晶体在不同温度下的吸收光谱和荧光光谱实验结果,研究发现由于电子-声子近共振耦合作用,Yb:FAP和Yb:C3S2-FAP晶体均存在有明显的振动谱,Yb:FAP晶体的零声子线在低温下还劈裂为相差10cm-1的两条线.采用激光选择激发技术研究了YB3+离子在FAP和C3S2-FAP晶体中的格位特征,结果表明YB3+离子在这两种基质中都只占据Ca(Ⅱ)格位,但由于CaF2的挥发,导致了Ca(Ⅱ)格位的局部畸变.
  • 加载中
  • 加载中
计量
  • 文章访问数:  424
  • HTML全文浏览数:  70
  • PDF下载数:  17
  • 施引文献:  0
出版历程

Yb:FAP和Yb:C3S2-FAP晶体光谱的温度特性和选择激发

  • 河南大学物理与信息光电子学院,开封,475001
  • 中国科学院上海光学精密机械研究所,上海,201800

摘要: 报导了Yb:FAP和Yb:C3S2-FAP晶体在不同温度下的吸收光谱和荧光光谱实验结果,研究发现由于电子-声子近共振耦合作用,Yb:FAP和Yb:C3S2-FAP晶体均存在有明显的振动谱,Yb:FAP晶体的零声子线在低温下还劈裂为相差10cm-1的两条线.采用激光选择激发技术研究了YB3+离子在FAP和C3S2-FAP晶体中的格位特征,结果表明YB3+离子在这两种基质中都只占据Ca(Ⅱ)格位,但由于CaF2的挥发,导致了Ca(Ⅱ)格位的局部畸变.

English Abstract