高级搜索

发光层厚度变化的高效红色有机电致磷光器件

,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

张晓波, 曹进, 委福祥, 蒋雪茵, 张志林, 朱文清, 许少鸿. 2006: 发光层厚度变化的高效红色有机电致磷光器件, 物理学报, 55(1): 119-124. doi: 10.3321/j.issn:1000-3290.2006.01.022
引用本文: 张晓波, 曹进, 委福祥, 蒋雪茵, 张志林, 朱文清, 许少鸿. 2006: 发光层厚度变化的高效红色有机电致磷光器件, 物理学报, 55(1): 119-124. doi: 10.3321/j.issn:1000-3290.2006.01.022
shu
Zhang Xiao-Bo, Cao Jin, Wei Fu-Xiang, Jiang Xue-Yin, Zhang Zhi-Lin, Zhu Wen-Qing, Xu Shao-Hong. 2006: High efficiency organic red electrophosphorescence devices with changing thickness of the emitting layer, Acta Physica Sinica, 55(1): 119-124. doi: 10.3321/j.issn:1000-3290.2006.01.022
Citation: Zhang Xiao-Bo, Cao Jin, Wei Fu-Xiang, Jiang Xue-Yin, Zhang Zhi-Lin, Zhu Wen-Qing, Xu Shao-Hong. 2006: High efficiency organic red electrophosphorescence devices with changing thickness of the emitting layer, Acta Physica Sinica, 55(1): 119-124. doi: 10.3321/j.issn:1000-3290.2006.01.022
shu

发光层厚度变化的高效红色有机电致磷光器件

  • 上海大学材料科学与工程学院,上海,201800

High efficiency organic red electrophosphorescence devices with changing thickness of the emitting layer

  • 摘要: 以铱配合物红色磷光体为掺杂剂,制备了基于TPBi材料的红色电致磷光器件,其结构为ITO/CuPc/NPB/TPBi:Btp2Ir(acac)/TPBi/Alq/LiF/Al.取得了在x=0.62,y=0.35的色度下,效率最高达2.43cd/A;电流密度为20mA/cm2时,亮度431cd/m2;电流密度为400mA/cm2时,亮度4798 cd/m2的结果.讨论了不同的发光层厚度影响器件色度和效率的主要因素:当发光层厚度小于15nm时,发光层中掺杂剂分子不能充分俘获从NPB HOMO能级上隧穿的空穴以及三线态激子之间相互作用导致的发光自猝灭是影响器件性能的主要原因;但当发光层厚度大于20nm时,无效的发光层以及发光层中的猝灭中心可能是造成器件效率下降的重要因素.
  • 加载中
  • 加载中
计量
  • 文章访问数:  377
  • HTML全文浏览数:  29
  • PDF下载数:  29
  • 施引文献:  0
出版历程
  • 刊出日期:  2006-01-30

发光层厚度变化的高效红色有机电致磷光器件

  • 上海大学材料科学与工程学院,上海,201800

摘要: 以铱配合物红色磷光体为掺杂剂,制备了基于TPBi材料的红色电致磷光器件,其结构为ITO/CuPc/NPB/TPBi:Btp2Ir(acac)/TPBi/Alq/LiF/Al.取得了在x=0.62,y=0.35的色度下,效率最高达2.43cd/A;电流密度为20mA/cm2时,亮度431cd/m2;电流密度为400mA/cm2时,亮度4798 cd/m2的结果.讨论了不同的发光层厚度影响器件色度和效率的主要因素:当发光层厚度小于15nm时,发光层中掺杂剂分子不能充分俘获从NPB HOMO能级上隧穿的空穴以及三线态激子之间相互作用导致的发光自猝灭是影响器件性能的主要原因;但当发光层厚度大于20nm时,无效的发光层以及发光层中的猝灭中心可能是造成器件效率下降的重要因素.