高级搜索

碳气凝胶薄片的制备及表面密度致密层去除工艺

,  ,  ,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

钟艳红, 周斌, 归佳寅, 杜艾, 徐翔, 朱秀榕, 吴广明, 张志华, 沈军. 2010: 碳气凝胶薄片的制备及表面密度致密层去除工艺, 强激光与粒子束, 22(12): 2875-2879. doi: 10.3788/HPLPB20102212.2875
引用本文: 钟艳红, 周斌, 归佳寅, 杜艾, 徐翔, 朱秀榕, 吴广明, 张志华, 沈军. 2010: 碳气凝胶薄片的制备及表面密度致密层去除工艺, 强激光与粒子束, 22(12): 2875-2879. doi: 10.3788/HPLPB20102212.2875
shu
Zhong Yanhong, Zhou Bin, Gui Jiayin, Du Ai, Xu Xiang, Zhu Xiurong, Wu Guangming, Zhang Zhihua, Shen Jun. 2010: Fabrication of carbon aerogel sheet and techniques of removing its dense layer, High Power Lase and Particle Beams, 22(12): 2875-2879. doi: 10.3788/HPLPB20102212.2875
Citation: Zhong Yanhong, Zhou Bin, Gui Jiayin, Du Ai, Xu Xiang, Zhu Xiurong, Wu Guangming, Zhang Zhihua, Shen Jun. 2010: Fabrication of carbon aerogel sheet and techniques of removing its dense layer, High Power Lase and Particle Beams, 22(12): 2875-2879. doi: 10.3788/HPLPB20102212.2875
shu

碳气凝胶薄片的制备及表面密度致密层去除工艺

  • 同济大学,上海市特殊人工微结构材料与技术重点实验室,上海,200092

Fabrication of carbon aerogel sheet and techniques of removing its dense layer

  • 摘要: 研究了不同密度和厚度的碳气凝胶薄片的制备及其表面致密层去除工艺.在以间苯二酚、甲醛为原料制备有机及碳气凝胶块体材料的基础上,结合自制活动式微模具成型工艺,制备了厚度在80～350 μm,密度在50～600 mg·cm-3范围内变化的碳气凝胶薄片.采用场发射扫描电镜、X射线相衬成像和表面轮廓仪-台阶仪等手段对其表面和内部微观结构进行了表征.测试结果表明,碳气凝胶薄片与块体的内部结构相同,但薄片表面存在一层和内部结构截然不同的致密层.采用不同粗糙程度的材料对薄片进行了表面微处理,成功去除该致密"皮"层.
  • 加载中
  • 加载中
计量
  • 文章访问数:  864
  • HTML全文浏览数:  227
  • PDF下载数:  98
  • 施引文献:  0
出版历程
  • 刊出日期:  2010-12-30

碳气凝胶薄片的制备及表面密度致密层去除工艺

  • 同济大学,上海市特殊人工微结构材料与技术重点实验室,上海,200092

摘要: 研究了不同密度和厚度的碳气凝胶薄片的制备及其表面致密层去除工艺.在以间苯二酚、甲醛为原料制备有机及碳气凝胶块体材料的基础上,结合自制活动式微模具成型工艺,制备了厚度在80～350 μm,密度在50～600 mg·cm-3范围内变化的碳气凝胶薄片.采用场发射扫描电镜、X射线相衬成像和表面轮廓仪-台阶仪等手段对其表面和内部微观结构进行了表征.测试结果表明,碳气凝胶薄片与块体的内部结构相同,但薄片表面存在一层和内部结构截然不同的致密层.采用不同粗糙程度的材料对薄片进行了表面微处理,成功去除该致密"皮"层.