高级搜索

Na2SrMg（PO4）2：Ce3+，Mn2+荧光粉的发光性质及其能量传递机理?

,  ,  , 

downloadPDF

上一篇

下一篇

熊晓波, 袁曦明, 刘金存, 宋江齐. 2015: Na2SrMg（PO4）2：Ce3+，Mn2+荧光粉的发光性质及其能量传递机理?, 物理学报, null(1): 017801. doi: 10.7498/aps.64.017801
引用本文: 熊晓波, 袁曦明, 刘金存, 宋江齐. 2015: Na2SrMg（PO4）2：Ce3+，Mn2+荧光粉的发光性质及其能量传递机理?, 物理学报, null(1): 017801. doi: 10.7498/aps.64.017801
shu
Xiong Xiao-Bo, Yuan Xi-Ming, Liu Jin-Cun, Song Jiang-Qi. 2015: Photoluminescence prop erties and energy transfer from Ce3+ to Mn2+ in Na2SrMg(PO4)2, Acta Physica Sinica, null(1): 017801. doi: 10.7498/aps.64.017801
Citation: Xiong Xiao-Bo, Yuan Xi-Ming, Liu Jin-Cun, Song Jiang-Qi. 2015: Photoluminescence prop erties and energy transfer from Ce3+ to Mn2+ in Na2SrMg(PO4)2, Acta Physica Sinica, null(1): 017801. doi: 10.7498/aps.64.017801
shu

Na2SrMg（PO4）2：Ce3+，Mn2+荧光粉的发光性质及其能量传递机理?

  • 中国地质大学材料与化学学院，教育部纳米矿物材料及应用工程研究中心，武汉 430074; 湖北警官学院实验中心，法庭科学湖北省重点实验室，武汉 430034

  • 中国地质大学材料与化学学院，教育部纳米矿物材料及应用工程研究中心，武汉 430074

Photoluminescence prop erties and energy transfer from Ce3+ to Mn2+ in Na2SrMg(PO4)2

  • 摘要: 采用高温固相法制备了Na2SrMg(PO4)2： Ce3+， Mn2+(NSMP：Ce3+， Mn2+)荧光粉，并对其发光性质及Ce3+对Mn2+的能量传递机理进行了研究。 Ce3+和Mn2+在334 nm和617 nm的发射峰分别为Ce3+的5d→4f跃迁和Mn2+的4T1(4G)→6A1(6S)跃迁产生。 Ce3+对Mn2+的发光有较强的敏化作用，根据Dexter能量传递效率公式判断Na2 SrMg(PO4)2中Ce3+对Mn2+的能量传递属于电偶极-电四极相互作用引起的共振能量传递。
    Abstract: Na2SrMg(PO4)2: Ce3+, Mn2+ phosphor was prepared by high temperature solid state reaction. Its luminescence properties and energy transfer from Ce3+ to Mn2+ were investigated. The emission bands of Ce3+ and Mn2+peaking at 334 nm and 617 nm were attributed to 5d→4f transition of Ce3+and 4T1(4G)→6A1(6S) transition of Mn2+, respectively. Dependence of Ce3+ and Mn2+ luminescence properties on their concentrations was investigated as well. With the increase of Mn2+ content, the emission intensity of Ce3+ could be observed to decrease, however, the emission intensity of Mn2+was found to increase. It is indicated that the luminescence of Mn2+could be sensitized by energy transfer from Ce3+ to Mn2+ in Na2SrMg(PO4)2 host. According to the Dexter’s energy transfer formula of multipolar interaction, it is demonstrated that the energy transfer between Ce3+ and Mn2+ is due to the electric dipole-quadripole interaction of the resonance transfer.
  • 加载中
  • 加载中
计量
  • 文章访问数:  393
  • HTML全文浏览数:  77
  • PDF下载数:  0
  • 施引文献:  0
出版历程
  • 刊出日期:  2015-01-15

Na2SrMg（PO4）2：Ce3+，Mn2+荧光粉的发光性质及其能量传递机理?

  • 中国地质大学材料与化学学院，教育部纳米矿物材料及应用工程研究中心，武汉 430074; 湖北警官学院实验中心，法庭科学湖北省重点实验室，武汉 430034
  • 中国地质大学材料与化学学院，教育部纳米矿物材料及应用工程研究中心，武汉 430074

摘要: 采用高温固相法制备了Na2SrMg(PO4)2： Ce3+， Mn2+(NSMP：Ce3+， Mn2+)荧光粉，并对其发光性质及Ce3+对Mn2+的能量传递机理进行了研究。 Ce3+和Mn2+在334 nm和617 nm的发射峰分别为Ce3+的5d→4f跃迁和Mn2+的4T1(4G)→6A1(6S)跃迁产生。 Ce3+对Mn2+的发光有较强的敏化作用，根据Dexter能量传递效率公式判断Na2 SrMg(PO4)2中Ce3+对Mn2+的能量传递属于电偶极-电四极相互作用引起的共振能量传递。