Nd含量对Bi6-xNdxFe1.4Ni0.6Ti3O18多晶材料多铁性的影响

,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

陈诚, 卢建安, 杜微, 王伟, 毛翔宇, 陈小兵. 2019: Nd含量对Bi6-xNdxFe1.4Ni0.6Ti3O18多晶材料多铁性的影响, 物理学报, 68(3): 248-257. doi: 10.7498/aps.68.20181287
引用本文: 陈诚, 卢建安, 杜微, 王伟, 毛翔宇, 陈小兵. 2019: Nd含量对Bi6-xNdxFe1.4Ni0.6Ti3O18多晶材料多铁性的影响, 物理学报, 68(3): 248-257. doi: 10.7498/aps.68.20181287
shu
Chen Cheng, Lu Jian-An, Du Wei, Wang Wei, Mao Xiang-Yu, Chen Xiao-Bing. 2019: Effects of Nd-doping on multiferroic properties of Bi6-xNdxFe1.4Ni0.6Ti3O1s polycrystalline, Acta Physica Sinica, 68(3): 248-257. doi: 10.7498/aps.68.20181287
Citation: Chen Cheng, Lu Jian-An, Du Wei, Wang Wei, Mao Xiang-Yu, Chen Xiao-Bing. 2019: Effects of Nd-doping on multiferroic properties of Bi6-xNdxFe1.4Ni0.6Ti3O1s polycrystalline, Acta Physica Sinica, 68(3): 248-257. doi: 10.7498/aps.68.20181287
shu

Nd含量对Bi6-xNdxFe1.4Ni0.6Ti3O18多晶材料多铁性的影响

  • 扬州大学物理科学与技术学院,扬州,225002

  • 扬州大学广陵学院,扬州,225127

Effects of Nd-doping on multiferroic properties of Bi6-xNdxFe1.4Ni0.6Ti3O1s polycrystalline

  • 摘要: 采用柠檬酸-硝酸盐法制备了Bi6-xNdxFe1.4Ni0.6Ti3O18 (BNFNT-x,x=0.00,0.10,0.20,0.25和0.30)前驱液,再经过干燥、烧结过程制备了单相多晶材料.研究发现,少量Nd掺杂有助于提高样品的铁电性能,BNFNT-0.25样品的铁电性能(2Pr)最大,约达到19.7 μC/cm2.室温下BNFNT-0.20样品磁性能(2Ms)最大约达到4.132 emu/g(1 emu/g=10-3 A.m2/g).变温介电损耗结果表明Nd掺杂降低了Fe3+和Fe2+间的电子转移或跃迁的激活能.X射线光电子能谱结果表明小量Nd掺杂有助于增强Bi离子稳定性,对改善样品的铁电性能有积极意义.
  • 加载中
  • 加载中
计量
  • 文章访问数:  63
  • HTML全文浏览数:  55
  • PDF下载数:  3
  • 施引文献:  0
出版历程

Nd含量对Bi6-xNdxFe1.4Ni0.6Ti3O18多晶材料多铁性的影响

  • 扬州大学物理科学与技术学院,扬州,225002
  • 扬州大学广陵学院,扬州,225127

摘要: 采用柠檬酸-硝酸盐法制备了Bi6-xNdxFe1.4Ni0.6Ti3O18 (BNFNT-x,x=0.00,0.10,0.20,0.25和0.30)前驱液,再经过干燥、烧结过程制备了单相多晶材料.研究发现,少量Nd掺杂有助于提高样品的铁电性能,BNFNT-0.25样品的铁电性能(2Pr)最大,约达到19.7 μC/cm2.室温下BNFNT-0.20样品磁性能(2Ms)最大约达到4.132 emu/g(1 emu/g=10-3 A.m2/g).变温介电损耗结果表明Nd掺杂降低了Fe3+和Fe2+间的电子转移或跃迁的激活能.X射线光电子能谱结果表明小量Nd掺杂有助于增强Bi离子稳定性,对改善样品的铁电性能有积极意义.