过渡金属原子掺杂对二维CrBr3电磁学性能的调控

,  , 

downloadPDF

上一篇

下一篇

陈旭凡, 杨强, 胡小会. 过渡金属原子掺杂对二维CrBr3电磁学性能的调控[J]. 物理学报, 2021, 70(24): 247401-1. doi: 10.7498/aps.70.20210936
引用本文: 陈旭凡, 杨强, 胡小会. 过渡金属原子掺杂对二维CrBr3电磁学性能的调控[J]. 物理学报, 2021, 70(24): 247401-1. doi: 10.7498/aps.70.20210936
shu
Xu-Fan Chen, Qiang Yang, Xiao-Hui Hu. Tunable electronic and magnetic properties of transition-metal atoms doped CrBr3 monolayer[J]. Acta Physica Sinica, 2021, 70(24): 247401-1. doi: 10.7498/aps.70.20210936
Citation: Xu-Fan Chen, Qiang Yang, Xiao-Hui Hu. Tunable electronic and magnetic properties of transition-metal atoms doped CrBr3 monolayer[J]. Acta Physica Sinica, 2021, 70(24): 247401-1. doi: 10.7498/aps.70.20210936
shu

过渡金属原子掺杂对二维CrBr3电磁学性能的调控

  • 1.

    南京工业大学材料科学与工程学院, 南京　211816

  • 2.

    南京工业大学, 江苏省先进无机功能复合材料协同创新中心, 南京　211816

    • 作者简介: 201961103025@njtech.edu.cn .
    通讯作者: E-mail: xiaohui.hu@njtech.edu.cn

  • 中图分类号: 74.78.-w, 68.55.Ln, 73.61.-r, 75.75.-c

Tunable electronic and magnetic properties of transition-metal atoms doped CrBr3 monolayer

  • 1.

    College of Materials Science and Engineering, Nanjing Tech University, Nanjing 211816, China

  • 2.

    Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing 211816, China

    • Corresponding author: E-mail: xiaohui.hu@njtech.edu.cn

  • MSC: 74.78.-w, 68.55.Ln, 73.61.-r, 75.75.-c

  • 摘要: 近年来, 二维铁磁材料由于其在自旋电子学领域中十分广阔的应用前景受到广泛关注. 单层CrBr3是具有本征铁磁性的半导体, 是自旋电子器件的潜在候选材料. 然而, 单层CrBr3的居里温度较低, 限制了其在自旋电子器件领域的应用. 本文基于密度泛函理论, 研究了3d过渡金属(TM)原子 (Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu和Zn)掺杂单层CrBr3的磁学和电学性能. 计算结果表明, TM原子掺杂后, 体系总磁矩呈现先增加再减小的趋势. 并且TM原子掺杂能够显著提高单层CrBr3的居里温度(TC), 实现了铁磁稳定性的增强. 其中, Sc掺杂CrBr3体系的TC与本征CrBr3相比提高了159%. 铁磁稳定性的增强归因于掺杂体系 (TM-CrBr3) 中直接交换和超交换相互作用之间的竞争. 此外, 依赖于不同的TM原子掺杂, TM-CrBr3体系表现出半金属性和自旋零带隙半导体性质. 本文的研究结果为单层CrBr3在纳米电子和自旋电子器件中的应用开辟了新的前景.
    Abstract: The CrBr3 monolayer is a two-dimensional semiconductor material with intrinsic ferromagnetism. However, the low Curie temperature of CrBr3 monolayer limits its practical development in innovative spintronic devices. The electronic and magnetic properties of transition-metal atoms doped CrBr3 monolayer have been systematically investigated by using the density functional theory calculations. The formation energy elucidates that all 3d transition metal (TM) atoms prefer to be doped in the middle of a hexagon (H) site of CrBr3 monolayer. And all the TM atoms, except the Zn atom, can bond strongly to the surrounding Cr atoms with sizable formation energy. The results also indicate that the magnetic moment of TM-CrBr3 system changes as a result of the charge transfer between TM atom and adjacent Cr atom. In addition, comparing with the intrinsic CrBr3, the TC of TM-CrBr3 system increases significantly, which means that the ferromagnetic stability of CrBr3 monolayer is enhanced. In particular, the TC of CrBr3 with Sc atom can be increased by 159%. The enhancement of ferromagnetism is mainly due to the competition between the direct exchange and the superexchange interaction. We also find that the electronic properties of the TM-CrBr3 systems are diverse. For example, Sc-, Ti-, V-, Mn-, Fe-, Co-, Ni-, Cu- and Zn-CrBr3 exhibit spin gapless semiconductor (SGS) properties with 100% spin polarization at Fermi level. The TM-CrBr3 system can be adjusted from semiconductor to half-metal when Cr atoms are doped into the CrBr3 monolayer. This work, together with recent achievements in the field of two-dimensional ferromagnetic materials, provides an experimentally achievable guide for realizing the preparation of TM-CrBr3 system with high Curie temperature. Moreover, the possibility of application of these systems in nanoelectronics and spintronics is increased.
  • 加载中

  • 图 1  (a) 单层CrBr3的结构示意图; (b) 单层CrBr3的能带结构和态密度. 能带结构中自旋向上和自旋向下分别用红色实线和蓝色实线表示

    Figure 1.  (a) Structural diagram of CrBr3 monolayer; (b) band structure and density of states of CrBr3 monolayer. The red and blue solid lines indicate spin-up and spin-down channels in the band structures, respectively.

    下载: 全尺寸图片 幻灯片

    图 2  (a)−(c) TM原子分别掺杂在H, Cr-Top和Br-Top位点时TM-CrBr3晶体结构的俯视图和侧视图; (d) TM-CrBr3的形成能; (e) 在H构型中, TM原子到CrBr3表层Br原子的高度以及TM原子与最邻近Br原子共价键的键长

    Figure 2.  Top and side views of the crystalline structure of three different doped positions of TM atoms labeled as (a) H, (b) Cr-Top and (c) Br-Top; (d) the formation energy of TM-CrBr3; (e) the height of the TM to Br on the surface of CrBr3 and the length of covalent bond between TM and nearest Br atom.

    下载: 全尺寸图片 幻灯片

    图 3  在300 K下, TM-CrBr3掺杂体系的H构型在5 ps后分子动力学模拟的结构示意图

    Figure 3.  Snapshots of TM-CrBr3 on the H site taken after 5 ps of DFT-MD simulations at 300 K.

    下载: 全尺寸图片 幻灯片

    图 4  (a) H构型的TM-CrBr3中TM原子的磁矩以及与TM原子最近邻的Cr原子的磁矩; (b) TM-CrBr3中Cr和TM原子的电荷转移; (c) TM-CrBr3体系的总磁矩(Mtotal)

    Figure 4.  (a) Magnetic moments of TM atom and Cr atom nearest to TM atom in TM-CrBr3 of H configuration; (b) charge transfer between Cr and TM atoms in TM-CrBr3; (c) the total magnetic moments (Mtotal) of TM-CrBr3.

    下载: 全尺寸图片 幻灯片

    图 5  (a) 本征CrBr3和TM-CrBr3体系的AFM构型与FM构型的能量差EAFM – EFM和居里温度TC; (b) 本征CrBr3和TM-CrBr3的Cr—Cr距离和Cr—I—Cr键角

    Figure 5.  (a) The EAFM – EFM and Curie temperature of pristine CrBr3 and TM-CrBr3; (b) the Cr—Cr distance and Cr—I—Cr bond angle in pristine CrBr3 and TM-CrBr3.

    下载: 全尺寸图片 幻灯片

    图 6  3d TM原子掺杂单层CrBr3的自旋极化能带结构, 插图是费米能级附近能带结构的放大图. 自旋向上和自旋向下分别用红色实线和蓝色实线表示

    Figure 6.  Spin-polarized band structures of 3d TM atoms doped CrBr3 monolayer. The illustration is an enlarged picture of the band structures near the Fermi level. The red and blue solid lines indicate spin-up and spin-down channels in the band structures, respectively.

    下载: 全尺寸图片 幻灯片

    表 1  本征CrBr3和TM-CrBr3体系中的交换耦合参数 (J )

    Table 1.  Exchange coupling parameter (J ) of pristine CrBr3 and TM-CrBr3.

    CrBr3ScTiVCrMnFeCoNiCuZn
    J/meV2.395.953.955.102.663.962.801.252.973.274.73
    下载: 导出CSV
  • [1] Hu X H, Björkman T, Lipsanen H, Sun L T, Krasheninnikov A V 2015 J. Phys. Chem. Lett. 6 3263 doi: 10.1021/acs.jpclett.5b01377
    [2] Hu X H, Wang Y F, Shen X D, Krasheninnikov A V, Sun L T, Chen Z F 2018 2D Mater. 5 031012 doi: 10.1088/2053-1583/aac859
    [3] Duan X D, Wang C, Pan A L, Yu R Q, Duan X F 2015 Chem. Soc. Rev. 44 8859 doi: 10.1039/C5CS00507H
    [4] Kou L Z, Ma Y D, Sun Z Q, Heine T, Chen C F 2017 J. Phys. Chem. Lett. 8 1905 doi: 10.1021/acs.jpclett.7b00222
    [5] Hu X H, Zhao Y H, Shen X D, Krasheninnikov A V, Chen Z F, Sun L T 2020 ACS Appl. Mater. Interfaces 12 26367 doi: 10.1021/acsami.0c05530
    [6] Ai W, Kou L Z, Hu X H, Wang Y F, Krasheninnikov A V, Sun L T, Shen X D 2019 J. Phys. Condens. Matter 31 445301 doi: 10.1088/1361-648X/ab29d8
    [7] Hu X H, Wan N, Sun L T, Krasheninnikov A V 2014 J. Phys. Chem. C 118 16133 doi: 10.1021/jp502365m
    [8] Hu X H, Zhang W, Sun L T, Krasheninnikov A V 2012 Phys. Rev. B 86 195418 doi: 10.1103/PhysRevB.86.195418
    [9] 艾雯, 胡小会, 潘林, 陈长春, 王一峰, 沈晓冬 2019 物理学报 68 197101 doi: 10.7498/aps.68.20190642 Ai W, Hu X H, Pan L, Chen C C, Wang Y F, Shen X D 2019 Acta Phys. Sin. 68 197101 doi: 10.7498/aps.68.20190642
    [10] Hu X H, Sun L T, Krasheninnikov A V 2012 Appl. Phys. Lett. 100 263115 doi: 10.1063/1.4731624
    [11] Zhang S L, Yan Z, Li Y F, Chen Z F, Zeng H B 2015 Angew. Chem. -Int. Ed. 54 3112 doi: 10.1002/anie.201411246
    [12] Chen X P, Yang Q, Meng R S, Jiang J K, Liang Q H, Tan C J, Sun X 2016 J. Mater. Chem. C 4 5434 doi: 10.1039/C6TC01141A
    [13] Yang Q, Kou L Z, Hu X H, Wang Y F, Lu C H, Krasheninnikov A V, Sun L T 2020 J. Phys. Condens. Matter 32 365302 doi: 10.1088/1361-648X/ab8ec9
    [14] Karthikeyan J, Komsa H P, Batzill M, Krasheninnikov A V 2019 Nano Lett. 19 4581 doi: 10.1021/acs.nanolett.9b01555
    [15] Yang Q, Hu X H, Shen X D, Krasheninnikov A V, Chen Z F, Sun L T 2021 ACS Appl. Mater. Interfaces 13 21593 doi: 10.1021/acsami.1c01701
    [16] Wang J X, Kou L Z, Ni Y R, Hu X H 2021 J. Phys. Condens. Matter 33 235502 doi: 10.1088/1361-648X/abea42
    [17] Kou L, Tang C, Guo W, Chen C 2011 ACS Nano 5 1012 doi: 10.1021/nn1024175
    [18] Liu L F, Kou L Z, Wang Y F, Lu C H, Hu X H 2020 Nanotechnology 31 455702 doi: 10.1088/1361-6528/abaa73
    [19] Tao P, Guo H H, Zhang Z D, Yang T 2014 J. Appl. Phys. 115 054305 doi: 10.1063/1.4864015
    [20] Jiang C H, Zhou R Q, Peng Z H, Zhu J F, Chen Q 2016 Phys. Chem. Chem. Phys. 18 32528 doi: 10.1039/C6CP06905C
    [21] Huang B, Clark G, Navarro-Moratalla E, Klein D R, Cheng R, Seyler K L, Zhong D, Schmidgall E, McGuire M A, Cobden D H, Yao W, Xiao D, Jarillo-Herrero P, Xu X D 2017 Nature 546 270 doi: 10.1038/nature22391
    [22] Gong C, Li L, Li Z L, Ji H W, Stern A, Xia Y, Cao T, Bao W, Wang C Z, Wang Y A, Qiu Z Q, Cava R J, Louie S G, Xia J, Zhang X 2017 Nature 546 265 doi: 10.1038/nature22060
    [23] Zhang Z W, Shang J Z, Jiang C Y, Rasmita A, Gao W B, Yu T 2019 Nano Lett. 19 3138 doi: 10.1021/acs.nanolett.9b00553
    [24] Chen W J, Sun Z Y, Wang Z J, Gu L H, Xu X D, Wu S W, Gao C L 2019 Science 366 983 doi: 10.1126/science.aav1937
    [25] Tang C L, Zhang Z W, Lai S, Tan Q H, Gao W B 2020 Adv. Mater. 32 1908498 doi: 10.1002/adma.201908498
    [26] Lyons T P, Gillard D, Molina-Sanchez A, Misra A, Withers F, Keatley P S, Kozikov A, Taniguchi T, Watanabe K, Novoselov K S, Fernandez-Rossier J, Tartakovskii A I 2020 Nat. Commun. 11 6021 doi: 10.1038/s41467-020-19816-4
    [27] Webster L, Yan J A 2018 Phys. Rev. B 98 144411 doi: 10.1103/PhysRevB.98.144411
    [28] Cheng Y C, Zhu Z Y, Mi W B, Guo Z B, Schwingenschlogl U 2013 Phys. Rev. 87 100401 doi: 10.1103/PhysRevB.87.100401
    [29] Li B, Xing T, Zhong M Z, Huang L, Lei N, Zhang J, Li J B, Wei Z M 2017 Nat. Commun. 8 1958 doi: 10.1038/s41467-017-02077-z
    [30] Peng Y T, Wei S Y, Xia C X, Jia Y 2013 Mod. Phys. Lett. B 27 1350204 doi: 10.1142/S0217984913502047
    [31] Song C S, Xiao W, Li L, Lu Y, Jiang P, Li C, Chen A X, Zhong Z C 2019 Phys. Rev. B 99 214435 doi: 10.1103/PhysRevB.99.214435
    [32] Guo Y L, Yuan S J, Wang B, Shi L, Wang J L 2018 J. Mater. Chem. C 6 5716 doi: 10.1039/C8TC01302K
    [33] Kresse G, Furthmuller J 1996 Phys. Rev. B 54 11169 doi: 10.1103/PhysRevB.54.11169
    [34] Kresse G, Furthmuller J 1996 Comput. Mater. Sci. 6 15 doi: 10.1016/0927-0256(96)00008-0
    [35] Blochl P E 1994 Phys. Rev. B 50 17953 doi: 10.1103/PhysRevB.50.17953
    [36] Perdew J P, Burke K, Ernzerhof M 1996 Phys. Rev. Lett. 77 3865 doi: 10.1103/PhysRevLett.77.3865
    [37] Chen S B, Huang C X, Sun H S, Ding J F, Jena P, Kan E 2019 J. Phys. Chem. C 123 17987 doi: 10.1021/acs.jpcc.9b04631
    [38] Tang C, Zhang L, Du A J 2020 J. Mater. Chem. C 8 14948 doi: 10.1039/D0TC04049E
    [39] Bacaksiz C, Sabani D, Menezes R M, Milosevic M V 2021 Phys. Rev. B 103 125418 doi: 10.1103/PhysRevB.103.125418
    [40] Zhang H, Yang W, Ning Y, Xu X H 2020 Nanoscale 12 13964 doi: 10.1039/D0NR02829K
    [41] 隋雪蕾 2017 博士学位论文 (北京: 清华大学) Sui X L 2017 Ph. D. Dissertation (Beijing: Tsinghua University) (in Chinese)
    [42] Krasheninnikov A V, Lehtinen P O, Foster A S, Pyykko P, Nieminen R M 2009 Phys. Rev. Lett. 102 126807 doi: 10.1103/PhysRevLett.102.126807
    [43] Sui X L, Si C, Shao B, Zou X L, Wu J, Gu B L, Duan W H 2015 J. Phys. Chem. C 119 10059 doi: 10.1021/jp5129468
    [44] Tiwari S, Van-de-Put M L, Soree B, Vandenberghe W G 2021 Phys. Rev. B 103 014432 doi: 10.1103/PhysRevB.103.014432
    [45] Goodenough J B 1955 Phys. Rev. 100 564 doi: 10.1103/PhysRev.100.564
    [46] Kanamori J 1960 J. Appl. Phys. 31 S14 doi: 10.1063/1.1984590
    [47] Anderson P W 1959 Phys. Rev. 115 2 doi: 10.1103/PhysRev.115.2
    [48] Wang X L 2008 Phys. Rev. Lett. 100 156404 doi: 10.1103/PhysRevLett.100.156404
  • 加载中
图( 6) 表( 1)
计量
  • 文章访问数:  102
  • HTML全文浏览数:  102
  • PDF下载数:  1
  • 施引文献:  0
出版历程
  • 收稿日期:  2021-05-17
  • 刊出日期:  2021-12-20

过渡金属原子掺杂对二维CrBr3电磁学性能的调控

    通讯作者: E-mail: xiaohui.hu@njtech.edu.cn
    作者简介: 201961103025@njtech.edu.cn
  • 1. 南京工业大学材料科学与工程学院, 南京　211816
  • 2. 南京工业大学, 江苏省先进无机功能复合材料协同创新中心, 南京　211816
  • 收稿日期:  2021-05-17

摘要: 近年来, 二维铁磁材料由于其在自旋电子学领域中十分广阔的应用前景受到广泛关注. 单层CrBr3是具有本征铁磁性的半导体, 是自旋电子器件的潜在候选材料. 然而, 单层CrBr3的居里温度较低, 限制了其在自旋电子器件领域的应用. 本文基于密度泛函理论, 研究了3d过渡金属(TM)原子 (Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu和Zn)掺杂单层CrBr3的磁学和电学性能. 计算结果表明, TM原子掺杂后, 体系总磁矩呈现先增加再减小的趋势. 并且TM原子掺杂能够显著提高单层CrBr3的居里温度(TC), 实现了铁磁稳定性的增强. 其中, Sc掺杂CrBr3体系的TC与本征CrBr3相比提高了159%. 铁磁稳定性的增强归因于掺杂体系 (TM-CrBr3) 中直接交换和超交换相互作用之间的竞争. 此外, 依赖于不同的TM原子掺杂, TM-CrBr3体系表现出半金属性和自旋零带隙半导体性质. 本文的研究结果为单层CrBr3在纳米电子和自旋电子器件中的应用开辟了新的前景.

English Abstract

    全文HTML

    1.   引　言

    • 近年来, 二维材料因其独特的性质, 在电子器件等领域具有巨大的应用潜力[1-12]. 然而, 诸如石墨烯、氮化硼和过渡金属硫族化合物等二维材料大多是非磁性的, 阻碍了其在自旋电子器件中的应用. 因此, 大量的工作致力于在非磁性的二维材料中引入磁性, 其中常见的方法有掺杂[13-15]、缺陷工程[16,17]、应变工程[18,19]和构建异质结[20]. 尽管可以通过各种调控手段在非磁性的二维材料中引入磁性, 但这种磁性通常是局部磁矩, 很难引入长程的铁磁有序. 因此, 开发具有固有铁磁有序的二维材料是十分必要的. 2017年, 华盛顿大学许晓栋课题组[21]和加州大学伯克利分校张翔课题组[22]各自独立地发现CrI3和Cr2Ge2Te6是具有长程铁磁序的二维材料, 这不仅为低维系统中磁性的基础研究开辟了新的途径, 而且为二维自旋电子学提供了新的机遇.

      单层CrBr3作为二维铁磁材料CrX3 (X = I, Br, Cl)中的一员, 已经在实验上被成功制备[23,24]. 单层CrBr3具有本征铁磁性和半导体性质, 是自旋电子器件的潜在候选者. 研究发现, 石墨烯/CrBr3范德瓦耳斯异质结由于其界面处磁场交换的可调控性, 有利于存储器件的应用[25]. 此外, 单层MoSe2与CrBr3接触后, 层间的电荷转移导致了磁光响应, 可用于新型光学探针的研发[26]. 但是, 单层CrBr3的居里温度TC仅有41 K[27], 远低于室温, 这极大地限制了其在自旋电子学领域的应用. 因此, 如何提高CrBr3的居里温度, 增强其铁磁稳定性是至关重要的问题.

      掺杂是调控二维材料电学和磁学性能的最常用方法之一. 例如, Cheng等[28]基于第一性原理方法预测了Mn, Fe, Co和Zn原子掺杂可以使单层MoS2产生磁性. Li等[29]采用化学气相输运法成功制备了铁掺杂的SnS2单晶, 利用振动样品磁强计观察到了铁磁性, 测得居里温度为31 K. 同样地, 第一性原理方法预测铜掺杂可以将单层ZnO转变为半金属铁磁体[30]. 碱金属掺杂显著增加了单层Cr2Ge2Te6的磁各向异性和居里温度, 实现了铁磁稳定性的增强[31]. 锂原子的掺杂可以提升CrI3体系的磁矩和居里温度, 从而实现CrI3铁磁稳定性的增强[32].

      本文基于密度泛函理论, 研究了3d过渡金属(TM)掺杂对单层CrBr3电学和磁学性能的影响. 研究发现, 过渡金属掺杂可以显著增强单层CrBr3的铁磁稳定性, 这主要归因于直接交换和超交换相互作用之间的竞争. 此外, 依赖于不同的TM原子掺杂, TM-CrBr3体系表现出半金属性和自旋零带隙半导体(spin gapless semiconductor, SGS)性质. 这些结果表明, 过渡金属掺杂是调控单层CrBr3电学和磁学性能的有效方法, 有助于推动单层CrBr3在纳米电子和自旋电子器件方面的应用.

    2.   计算方法

    • 本文使用VASP[33,34] (Vienna ab initio simulation package)软件包中的投影缀加波[35]进行密度泛函理论(density functional theory, DFT)计算. 采用Perdew-Burke-Ernzerhof [36]的广义梯度近似泛函来描述电子交换关联能. 平面波的截断能设置为400 eV, 总能和力的收敛分别小于10–6 eV和0.01 eV/Å. 采用7 × 7 × 1的K点网格进行几何优化和自洽计算. 引入至少18 Å的真空层来避免周期性边界结构中层与层之间的相互作用. 采用基于Ising模型的蒙特卡罗模拟[37,38]来估算本征CrBr3和掺杂体系的居里温度. 海森伯自旋哈密顿量可表示为

      其中J为最近邻的交换耦合参数; $ {S}_{i/j} $表示与z方向平行或反平行的自旋. J值可由以下公式获得

      其中$ {E}_{\rm{e}\rm{x}} $是单层CrBr3的Néel-AFM和FM之间的能量差,

      S = 3/2为每个Cr原子的净磁矩 [39].

    3.   结果与讨论

    • 单层CrBr3属于$ R\overline{3} $空间群的BiI3结构, 以Br原子为中心与Cr原子形成了[CrBr6]共边八面体, Cr-Br-Cr的层状结构沿c轴堆叠, 如图1(a)所示. 单层CrBr3优化后的晶格常数为6.44 Å, Cr—Br键的键长为2.52 Å, 与以前的报道一致[27,40]. 由单层CrBr3的能带结构和态密度图(图1(b))可知, 单层CrBr3是间接带隙半导体, 禁带宽度为1.31 eV. 其导带底和价带顶主要由Cr原子的3d和Br原子的5p轨道贡献. 考虑了4种不同的磁构型用于确定单层CrBr3的磁基态, 分别为铁磁(FM)和3个反铁磁 (Néel-AFM, Zigzag-AFM, Stripy-AFM), 并计算了它们的能量. 计算结果表明, 单层CrBr3在铁磁构型下的能量最低, 每个Cr原子具有3.00 μB的磁矩.

      首先, 选取了2 × 2 × 1的CrBr3超胞来构建3d过渡金属 (TM = Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu和Zn) 掺杂单层CrBr3的模型结构. 根据CrBr3的结构特点, 考虑了3种可能的过渡金属原子掺杂位点: Br原子构成的六元环中心(H), Cr原子的上方(Cr-Top) 和Br原子的上方(Br-Top), 如图2(a)—(c)所示. 通过比较不同掺杂位点对应的TM-CrBr3结构的形成能, 确定最稳定的模型结构. 形成能定义为

      其中$ {E}_{{\rm{C}\rm{r}\rm{B}\rm{r}}_{3} + \rm{T}\rm{M}} $是TM原子掺杂CrBr3结构优化后的总能量, $ {E}_{{\rm{C}\rm{r}\rm{B}\rm{r}}_{3}} $是本征CrBr3的总能量, $ {\mu }_{\rm{T}\rm{M}} $是孤立TM二聚体中TM原子的化学势.

      根据形成能的定义, 掺杂体系的形成能越低, 稳定性越高. 图2(d)是不同掺杂位点对应的TM-CrBr3的形成能, 发现相比Cr-Top和Br-Top位点, H位点对应的TM-CrBr3的形成能最低, 这意味着3d TM原子掺杂在CrBr3的H位点时体系更稳定. 因此, 在后续的讨论中, 将研究重点放在H构型的TM-CrBr3体系. 从图2(d)看出TM-CrBr3 (Zn除外)的形成能较低(–1.19 至 –5.32 eV), 表明TM-CrBr3的稳定性较强. 其中, Sc-CrBr3具有最低的形成能(–5.32 eV), 表明Sc-CrBr3的结构最稳定. 而对于满壳层的Zn原子而言, 最外层的12个电子完全填满了3d和4s轨道, 因此, Zn与单层CrBr3的结合较弱, 形成能最高(–0.47 eV), 体系结构的稳定性较差. 进一步, 基于DFT的分子动力学模拟(DFT-MD), 研究了TM-CrBr3掺杂体系H构型在300 K的热稳定性. 结果表明, H构型在5 ps后晶体结构保持稳定(图3). 此外, 在H构型中, TM原子与最邻近的6个Br原子以共价键的形式连接, TM—Br的键长为2.59—2.68 Å, TM原子到CrBr3表面的高度h在1.45—1.54 Å的范围内 (如图2(e)所示).

      接下来, 研究了TM-CrBr3的磁学性能. 为了便于描述, 将Cr原子的磁矩、TM原子的磁矩和TM-CrBr3的总磁矩分别命名为MCr, MTM和Mtotal. 与本征CrBr3的MCr (3.00 μB) 相比, TM-CrBr3中与TM原子最邻近Cr原子的MCr有所增加(3.08 μB—3.31 μB), 如图4(a)所示. 产生这种现象的原因是Cr原子获得了来自于TM原子的部分电荷(图4(b)). 不同的TM原子之间存在电负性的差异, 即TM原子在化合物中吸引电子的能力不同, 导致了TM-CrBr3中电荷转移的差异. 在所有TM-CrBr3中, Sc-CrBr3中Cr原子获得的电荷最多, 约为0.06 e, 因而对应的MCr最大 (3.31 μB). 与Sc-CrBr3相反, Cu-CrBr3中Cr原子获得的电荷最少, 约为0.02 e, 所以MCr最小 (3.08 μB).

      在TM-CrBr3体系中, 磁性原子为Cr和TM原子, 总磁矩(Mtotal)主要由Cr原子贡献, 部分来源于TM原子. 根据Mtotal的变化趋势(图4(c)), 掺杂体系可分为3类. 1) Sc, Ti, V, Cr, Mn掺杂的CrBr3体系, 其Mtotal大于本征CrBr3的Mtotal (24 μB), 随着掺杂元素原子序数的增加 (从Sc到Mn), 其Mtotal是线性增加的. 进一步的观察发现, 掺杂体系中增加的磁矩与掺杂TM原子的最外层电子数有关, 如图4(c)所示. 例如, Sc最外层的4s和3d轨道的电子共有3个, 因此, Sc-CrBr3体系的Mtotal (27 μB) 比本征CrBr3的总磁矩 (24 μB) 增加了3 μB. 随着TM原子序数的增加, 到Mn原子时, 最外层的4s和3d轨道的电子数线性增加到7, 此时掺杂体系的Mtotal从27 μB线性增加到31 μB (从Sc到Mn). 2) Fe-CrBr3, Co-CrBr3和Ni-CrBr3体系的Mtotal为分数, 整体大致呈现为线性下降趋势, Mtotal分别为29.08 μB, 27.43 μB和26.69 μB. 3) Cu-CrBr3和Zn-CrBr3体系, Mtotal分别为25 μB和26 μB. 在Cu-CrBr3体系中, Cu原子最外层共有11个电子, 其中10个电子填满了所有的3d轨道[41], 剩下的一个未配对的游离电子贡献了磁矩, 使Mtotal比本征CrBr3的总磁矩增加了1 μB. 对于Zn-CrBr3体系, Zn原子最外层3d和4s轨道被12个电子完全填充, 导致Zn原子的净磁矩为零, 因此Zn-CrBr3体系的Mtotal几乎完全来自于Cr原子. 总的来说, 随着TM原子序数的增加, 掺杂体系的Mtotal大致呈现先增加, 再减小的趋势. 在3d过渡金属掺杂单层CrI3, MoSe2和磷烯的研究中, 也发现了类似的变化趋势[15,42,43].

      接下来, 进一步研究了TM-CrBr3体系的铁磁稳定性. 采用了基于Ising模型的蒙特卡罗模拟方法, 对TM-CrBr3的居里温度(TC)进行了计算, 以此来反映TM-CrBr3体系铁磁耦合的稳定性. 本征CrBr3和TM-CrBr3中的交换耦合参数(J )的具体数值见表1. 计算得到本征CrBr3的J值为2.39 meV, 与之前的研究结果一致[27]. 通过计算得到的J值, 计算了单层本征CrBr3的居里温度, 计算结果表明, 单层CrBr3的TC为41 K, 与之前的计算结果一致[27,44]. TM-CrBr3体系的铁磁(FM)构型与反铁磁(AFM)构型的能量差 (EAFM – EFM), 以及TM-CrBr3的TC, 如图5(a)所示. 从图5(a)可以看出, 除Co-CrBr3以外, 其他掺杂体系的能量差为144—322 meV, TC为46—106 K, 与本征CrBr3的TC相比, 均有所增加. 其中, Sc, V和Zn掺杂CrBr3的TC显著增加. 特别地, ScCrBr3的TC增加了159%. 这些结果表明, 3d过渡金属 (Co除外) 掺杂能够增强单层CrBr3的铁磁稳定性.

      单层CrBr3的铁磁耦合可以根据Goodenough-Kanamori-Anderson规则[45-47]来解释. 直接交换相互作用会受到相邻Cr原子之间的直接电子跃迁的影响, 与Cr原子之间距离d相关, 反铁磁耦合通常随着距离d的减小而增强. 超交换相互作用主要源于Cr的d轨道和Br的p轨道重叠, 由Cr—Br—Cr键角θ决定, 键角θ越接近90°, 则铁磁耦合越强. 体系的磁基态由直接交换和超交换相互作用之间的竞争决定. 图5(b)给出了TM-CrBr3体系中的Cr—Cr距离和Cr—Br—Cr键角的变化. 相比于本征CrBr3, TM原子(除Co以外)掺杂后, TM-CrBr3体系的Cr—Br—Cr键角更接近90°, Cr原子之间的距离d增大, 导致影响铁磁耦合的超交换相互作用增强, 影响反铁磁耦合的直接交换相互作用减弱. 因此, TM原子 (除Co以外) 掺杂CrBr3的铁磁稳定性显著增强. 对于Co-CrBr3, 相较于本征CrBr3, Cr原子之间距离d几乎不变, 然而Cr—Br—Cr键角增大了1°, 导致Co-CrBr3中影响铁磁耦合的超交换相互作用减弱. 因此, 与本征CrBr3相比, Co-CrBr3的铁磁稳定性减弱.

      最后, 研究了过渡金属原子掺杂对单层CrBr3电学性质的影响, TM-CrBr3体系的能带结构, 如图6所示. 在Cr-CrBr3体系中, 自旋向上和自旋向下的通道分别表现出金属性和半导体性, 因此, Cr原子掺杂使CrBr3从半导体转变为半金属, 能够实现100%自旋极化的电流. 在Sc-CrBr3掺杂体系中, 其自旋向上和自旋向下的带隙值分别为0.06 eV和2.37 eV. 根据Wang[48]的定义, SGS是指能带结构中的一个自旋方向表现为零带隙, 另一个自旋方向表现出半导体性质; 或者两个自旋方向的通道都有带隙, 但是其中一个自旋通道的导带与另一个自旋通道的价带之间是零带隙. 这里的“零带隙”是指能带间隙等于或小于0.1 eV. 在Sc-CrBr3体系的能带结构中, 自旋向上通道的带隙值为2.37 eV, 自旋向下通道的带隙值为0.06 eV, 因此, Sc-CrBr3可以称为SGS. 在SGS材料中, 电子无需能量就可以从价带跃迁到导带, 从而在费米能级处产生100%的自旋极化, 因此, 这种材料可以作为理想的自旋电子器件候选材料. 同样地, 在除Cr-CrBr3以外的其他TM-CrBr3 (Sc-, Ti-, V-, Mn-, Fe-, Co-, Ni-, Cu-和Zn-CrBr3)体系中, 发现其中一个自旋通道的带隙小于0.1 eV, 表现为SGS性质. 上述结果表明, 依赖于不同的TM原子掺杂, TM-CrBr3体系表现出半金属性或SGS性质, 3d过渡金属原子的掺杂可以使CrBr3在纳米电子器件中具有潜在的应用价值.

    4.   结　论

    • 通过系统的DFT计算, 研究了3d过渡金属掺杂对单层CrBr3的稳定性, 电学性能和磁学性能的影响. 研究结果表明, 相比Cr-Top和Br-Top位点, TM-CrBr3体系在H位点形成能更低, 结构更稳定. 在磁学性能方面, 过渡金属原子掺杂后的电荷转移, 导致了TM-CrBr3体系磁矩发生变化, Mtotal随着TM原子序数的增加, 大致呈现先增加再减小的趋势. 并且, 过渡金属原子掺杂可以提高CrBr3的居里温度. 其中, Sc原子掺杂使体系的居里温度提高了159%, 铁磁稳定性显著增强. TM-CrBr3掺杂体系铁磁稳定性的增强主要归因于直接交换和超交换相互作用之间的竞争. 此外, 依赖于不同的TM原子掺杂, TM-CrBr3体系表现出半金属性和SGS性质: 除Cr以外, 其他TM掺杂CrBr3体系表现为SGS性质; Cr-CrBr3体系具有半金属性. 本文的研究结果表明, 过渡金属掺杂是增强单层CrBr3铁磁稳定性并调控其电学性能的有效策略, 为基于CrBr3自旋电子器件的实验研究提供了理论基础, 并且极大地促进了CrBr3在纳米电子和自旋电子器件中的应用.

      感谢南京工业大学高性能计算中心的计算支持.