高级搜索

25 MeV/u Kr辐照下PET薄膜的损伤机制研究

,  ,  ,  ,  ,  ,  ,  ,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

彭书赋, 孙友梅, 罗捷, 常海龙, 刘杰, 侯明东, 段敬来, 姚会军, 莫丹, 张苓, 尹经敏, 陈艳峰, 翟鹏飞, 曹殿亮. 2010: 25 MeV/u Kr辐照下PET薄膜的损伤机制研究, 原子核物理评论, 27(1): 97-101.
引用本文: 彭书赋, 孙友梅, 罗捷, 常海龙, 刘杰, 侯明东, 段敬来, 姚会军, 莫丹, 张苓, 尹经敏, 陈艳峰, 翟鹏飞, 曹殿亮. 2010: 25 MeV/u Kr辐照下PET薄膜的损伤机制研究, 原子核物理评论, 27(1): 97-101.
shu
PENG Shu-fu, SUN You-mei, LUO Jie, CHANG Hai-long, LIU Jie, HOU Ming-dong, DUAN Jing-lai, YAO Hui-jun, MO Dan, ZHANG Ling, YIN Jin-ming, CHEN Yan-feng, ZHAI Peng-fei, CAO Dian-liang. 2010: Damage Mechanism of PET Irradiated by 25 MeV/u Kr Ions, Nuclear Physics Review, 27(1): 97-101.
Citation: PENG Shu-fu, SUN You-mei, LUO Jie, CHANG Hai-long, LIU Jie, HOU Ming-dong, DUAN Jing-lai, YAO Hui-jun, MO Dan, ZHANG Ling, YIN Jin-ming, CHEN Yan-feng, ZHAI Peng-fei, CAO Dian-liang. 2010: Damage Mechanism of PET Irradiated by 25 MeV/u Kr Ions, Nuclear Physics Review, 27(1): 97-101.
shu

25 MeV/u Kr辐照下PET薄膜的损伤机制研究

  • 中国科学院近代物理研究所,甘肃,兰州,730000;中国科学院研究生院,北京,100049

  • 中国科学院近代物理研究所,甘肃,兰州,730000

Damage Mechanism of PET Irradiated by 25 MeV/u Kr Ions

  • 摘要: 通过25 MeV/u ~(86)Kr离子辐照叠层结晶聚对苯二甲酸乙二醇酯膜(PET),在不同的电子能损(3.40-7.25 keV/nm)和离子注量(5×10~(11)-3×10~(12) ions/cm~2)辐照条件下,对Kr离子在PET中引起的辐照损伤效应进行了研究.借助傅里叶变换红外光谱分析,通过对样品的红外吸收峰进行扣除基底后的Lorentz拟合,分析了与主要官能团对应的吸收峰强度的变化趋势,研究了化学结构与组分在重离子辐照下的变化规律;利用X射线衍射光谱仪测量,研究了Kr离子在PET潜径迹中引起的非晶化过程,并通过对吸光度和非晶化强度随离子注量的指数衰减规律的分析,获得了不同电子能损离子辐照PET时主要官能团的损伤截面和非晶化截面及对应的潜径迹半径.
    Abstract: At room temperature,polyethylene terephthalate(PET)foil stacks were irradiated by 25 MeV/u Kr ions in the electronic stopping power range(3.3-7.66 keV/nm)and the fluence range from 5 ×10~(11) to 3×10~(12) ions/cm~2.The behaviour of the main function groups with fluence and electronic stopping power were studied by using Fourier-transform-infrared(FTIR)spectroscopy,the degradation of the function group was investigated with the Lorentz fitting subtracted baseline.The amorphous processes in the latent tracks of PET were studied by X-ray diffraction(XRD)measurements.The Kr ion induced degradation cross-section and amorphisation cross-sections(radii)for different electronic energy loss were acquired from the experimental data(FT-IR and XRD)by exponential decay function respectively.
  • 加载中
  • 加载中
计量
  • 文章访问数:  441
  • HTML全文浏览数:  38
  • PDF下载数:  0
  • 施引文献:  0
出版历程
  • 刊出日期:  2010-03-20

25 MeV/u Kr辐照下PET薄膜的损伤机制研究

  • 中国科学院近代物理研究所,甘肃,兰州,730000;中国科学院研究生院,北京,100049
  • 中国科学院近代物理研究所,甘肃,兰州,730000

摘要: 通过25 MeV/u ~(86)Kr离子辐照叠层结晶聚对苯二甲酸乙二醇酯膜(PET),在不同的电子能损(3.40-7.25 keV/nm)和离子注量(5×10~(11)-3×10~(12) ions/cm~2)辐照条件下,对Kr离子在PET中引起的辐照损伤效应进行了研究.借助傅里叶变换红外光谱分析,通过对样品的红外吸收峰进行扣除基底后的Lorentz拟合,分析了与主要官能团对应的吸收峰强度的变化趋势,研究了化学结构与组分在重离子辐照下的变化规律;利用X射线衍射光谱仪测量,研究了Kr离子在PET潜径迹中引起的非晶化过程,并通过对吸光度和非晶化强度随离子注量的指数衰减规律的分析,获得了不同电子能损离子辐照PET时主要官能团的损伤截面和非晶化截面及对应的潜径迹半径.