高级搜索

激光熔覆 FeCrNiMnMox B0.5高熵合金涂层组织与耐蚀性能

,  , 

downloadPDF

上一篇

下一篇

李栋梁, 周芳, 余师豪. 2016: 激光熔覆 FeCrNiMnMox B0.5高熵合金涂层组织与耐蚀性能, 强激光与粒子束, null(2): 029001. doi: 10.11884/HPLPB201628.029001
引用本文: 李栋梁, 周芳, 余师豪. 2016: 激光熔覆 FeCrNiMnMox B0.5高熵合金涂层组织与耐蚀性能, 强激光与粒子束, null(2): 029001. doi: 10.11884/HPLPB201628.029001
shu
Li Dongliang, Zhou Fang, Yu Shihao. 2016: Microstrucrure and corrosion resistance of FeCrNiMnMox B0.5 high entropy alloy coating prepared by laser cladding, High Power Lase and Particle Beams, null(2): 029001. doi: 10.11884/HPLPB201628.029001
Citation: Li Dongliang, Zhou Fang, Yu Shihao. 2016: Microstrucrure and corrosion resistance of FeCrNiMnMox B0.5 high entropy alloy coating prepared by laser cladding, High Power Lase and Particle Beams, null(2): 029001. doi: 10.11884/HPLPB201628.029001
shu

激光熔覆 FeCrNiMnMox B0.5高熵合金涂层组织与耐蚀性能

  • 贵州大学 材料与冶金学院,贵阳,550025

Microstrucrure and corrosion resistance of FeCrNiMnMox B0.5 high entropy alloy coating prepared by laser cladding

  • 摘要: 为了获得性能优异的涂层材料,采用激光熔覆的方法在 Q235钢基体上制备了不同 Mo 含量的FeCrNiMnMoB0.5系高熵合金涂层,着重探究 Mo 对高熵合金组织与性能的影响。通过金相、X 射线衍射、扫描电镜、硬度计、电化学工作站分别研究了高熵合金涂层的显微组织、相结构、显微硬度及耐蚀性能。结果表明：FeCrNiMnMoB0.5系高熵合金组织为树枝晶,主要由 fcc 相和少量金属间化合物构成。当添加少量 Mo 时,涂层的硬度较低,为290 HV,随着 Mo 的增加,晶格畸变加剧,出现少量金属化合物,涂层硬度最大增加到658 HV。在模拟饱和盐水泥浆溶液中 FeCrNiMnMo0.4 B0.5表现出较好的耐腐蚀性。
    Abstract: In order to obtain excellent coating materials,FeCrNiMnMoB0.5 high entropy alloy coatings were prepared on Q235 steel by laser cladding.The effect of Mo on microstructure and properties of high entropy alloy coatings have been investiga-ted emphatically.By means of optical microscope,X-ray diffraction,scanning electron microscope,hardness tester and electro-chemical workstation,the microstructure,phase structure,hardness and corrosion resistance were studied.Results show that the microstructure of FeCrNiMnMoB0.5 high entropy alloy coatings is dendrites and the coating is mainly composed of fcc phase and a small amount of intermetallic compounds.After adding a small amount of Mo,the average hardness is very low,about 290 HV. With the increase of Mo,lattice distortion is enhanced and metal compounds appear.The hardness of the coating reaches a maxi-mum of 658 HV.Polarization curves indicate that FeCrNiMnMo0.4 B0.5 shows good corrosion resistance in the saturated salt mud solution.
  • 加载中
  • 加载中
计量
  • 文章访问数:  350
  • HTML全文浏览数:  104
  • PDF下载数:  83
  • 施引文献:  0
出版历程
  • 刊出日期:  2016-02-28

激光熔覆 FeCrNiMnMox B0.5高熵合金涂层组织与耐蚀性能

  • 贵州大学 材料与冶金学院,贵阳,550025

摘要: 为了获得性能优异的涂层材料,采用激光熔覆的方法在 Q235钢基体上制备了不同 Mo 含量的FeCrNiMnMoB0.5系高熵合金涂层,着重探究 Mo 对高熵合金组织与性能的影响。通过金相、X 射线衍射、扫描电镜、硬度计、电化学工作站分别研究了高熵合金涂层的显微组织、相结构、显微硬度及耐蚀性能。结果表明：FeCrNiMnMoB0.5系高熵合金组织为树枝晶,主要由 fcc 相和少量金属间化合物构成。当添加少量 Mo 时,涂层的硬度较低,为290 HV,随着 Mo 的增加,晶格畸变加剧,出现少量金属化合物,涂层硬度最大增加到658 HV。在模拟饱和盐水泥浆溶液中 FeCrNiMnMo0.4 B0.5表现出较好的耐腐蚀性。