高级搜索

熔石英表面铜颗粒污染激光诱导损伤

,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

苗心向, 程晓锋, 袁晓东, 吕海兵, 叶亚云, 贺少勃, 郑万国. 2010: 熔石英表面铜颗粒污染激光诱导损伤, 强激光与粒子束, 22(8): 1740-1744. doi: 10.3788/HPLPB201002208.1740
引用本文: 苗心向, 程晓锋, 袁晓东, 吕海兵, 叶亚云, 贺少勃, 郑万国. 2010: 熔石英表面铜颗粒污染激光诱导损伤, 强激光与粒子束, 22(8): 1740-1744. doi: 10.3788/HPLPB201002208.1740
shu
Miao Xinxiang, Cheng Xiaofeng, Yuan Xiaodong, Lü Haibing, Ye Yayun, He Shaobo, Zheng Wanguo. 2010: Laser-induced damage of fused silica initiated by Cu contamination particles on surface, High Power Lase and Particle Beams, 22(8): 1740-1744. doi: 10.3788/HPLPB201002208.1740
Citation: Miao Xinxiang, Cheng Xiaofeng, Yuan Xiaodong, Lü Haibing, Ye Yayun, He Shaobo, Zheng Wanguo. 2010: Laser-induced damage of fused silica initiated by Cu contamination particles on surface, High Power Lase and Particle Beams, 22(8): 1740-1744. doi: 10.3788/HPLPB201002208.1740
shu

熔石英表面铜颗粒污染激光诱导损伤

  • 中国工程物理研究院,激光聚变研究中心,四川,绵阳,621900

Laser-induced damage of fused silica initiated by Cu contamination particles on surface

  • 摘要: 利用SAGA-S激光器输出的355 nm波长激光,研究了熔石英表面铜颗粒污染的激光损伤规律.采用磁控溅射的方式在洁净熔石英表面制备不同尺寸的颗粒状污染物,用1-on-1,10-on-1,20-on-1的方式测试经污染后的熔石英基底的损伤阈值,并采用光学显微镜观察损伤形貌、CCD在线测量损伤斑尺寸.结果表明:污染后的熔石英基底的损伤主要发生在后表面,而且以热烧蚀和热应力为主,基底的损伤阈值与熔石英前表面污染颗粒尺寸呈负指数关系,随后表面污染物颗粒尺寸的增大呈略微下降.前表面颗粒污染物诱导损伤斑尺寸为颗粒污染物尺寸的4倍,后表面颗粒污染物引起的损伤斑尺寸约为颗粒污染物尺寸的2倍.并绘出损伤斑尺寸与颗粒尺寸、辐照方式之间的关系.
  • 加载中
  • 加载中
计量
  • 文章访问数:  557
  • HTML全文浏览数:  76
  • PDF下载数:  33
  • 施引文献:  0
出版历程
  • 刊出日期:  2010-08-30

熔石英表面铜颗粒污染激光诱导损伤

  • 中国工程物理研究院,激光聚变研究中心,四川,绵阳,621900

摘要: 利用SAGA-S激光器输出的355 nm波长激光,研究了熔石英表面铜颗粒污染的激光损伤规律.采用磁控溅射的方式在洁净熔石英表面制备不同尺寸的颗粒状污染物,用1-on-1,10-on-1,20-on-1的方式测试经污染后的熔石英基底的损伤阈值,并采用光学显微镜观察损伤形貌、CCD在线测量损伤斑尺寸.结果表明:污染后的熔石英基底的损伤主要发生在后表面,而且以热烧蚀和热应力为主,基底的损伤阈值与熔石英前表面污染颗粒尺寸呈负指数关系,随后表面污染物颗粒尺寸的增大呈略微下降.前表面颗粒污染物诱导损伤斑尺寸为颗粒污染物尺寸的4倍,后表面颗粒污染物引起的损伤斑尺寸约为颗粒污染物尺寸的2倍.并绘出损伤斑尺寸与颗粒尺寸、辐照方式之间的关系.