沈龙光, 张庆茂, 宋杰, 廖健宏. 2009: 铁基合金激光熔覆层的高温磨损性能, 强激光与粒子束, 21(5): 658-662.
引用本文: 沈龙光, 张庆茂, 宋杰, 廖健宏. 2009: 铁基合金激光熔覆层的高温磨损性能, 强激光与粒子束, 21(5): 658-662.
shu
Shen Longguang, Zhang Qingmao, Song Jie, Liao Jianhong. 2009: Wear performance of Fe-based alloy strengthened by laser cladding under high temperature, High Power Lase and Particle Beams, 21(5): 658-662.
Citation: Shen Longguang, Zhang Qingmao, Song Jie, Liao Jianhong. 2009: Wear performance of Fe-based alloy strengthened by laser cladding under high temperature, High Power Lase and Particle Beams, 21(5): 658-662.
shu

铁基合金激光熔覆层的高温磨损性能

  • 华南师范大学,激光加工技术实验室,广州,510006

Wear performance of Fe-based alloy strengthened by laser cladding under high temperature

  • 摘要: 为提高40Cr钢表面耐磨性,采用预置激光熔覆法在40Cr基体表面制备Fe基涂层,利用HT-500摩擦磨损实验机测定干摩擦条件下,基体和熔覆层的摩擦因数随温度变化的规律.利用表面粗糙度轮廓仪测量磨痕的深度和宽度,SEM观察熔覆层以及磨痕的显微组织形貌,使用HV-1000型显微硬度仪检测基体和熔覆层结合部分的硬度.研究结果表明:熔覆层平均显微硬度值达到373.8HV(0.2);显著高于基体硬度198.4HV(0.2).在干摩擦条件下,随着温度升高,磨损过程逐渐变平缓,平均摩擦因数降低,磨损率增加,耐磨性下降;在350～400 ℃之间,熔覆层磨损性能优于基体.
  • 加载中
  • 加载中
计量
  • 文章访问数:  421
  • HTML全文浏览数:  27
  • PDF下载数:  148
  • 施引文献:  0
出版历程
  • 刊出日期:  2009-05-30

铁基合金激光熔覆层的高温磨损性能

  • 华南师范大学,激光加工技术实验室,广州,510006

摘要: 为提高40Cr钢表面耐磨性,采用预置激光熔覆法在40Cr基体表面制备Fe基涂层,利用HT-500摩擦磨损实验机测定干摩擦条件下,基体和熔覆层的摩擦因数随温度变化的规律.利用表面粗糙度轮廓仪测量磨痕的深度和宽度,SEM观察熔覆层以及磨痕的显微组织形貌,使用HV-1000型显微硬度仪检测基体和熔覆层结合部分的硬度.研究结果表明:熔覆层平均显微硬度值达到373.8HV(0.2);显著高于基体硬度198.4HV(0.2).在干摩擦条件下,随着温度升高,磨损过程逐渐变平缓,平均摩擦因数降低,磨损率增加,耐磨性下降;在350～400 ℃之间,熔覆层磨损性能优于基体.