两种纤维增强复合材料连续激光烧蚀阈值测量及吸收特性分析

,  ,  , 

downloadPDF

上一篇

下一篇

张永强, 王贵兵, 唐小松, 王伟平. 2009: 两种纤维增强复合材料连续激光烧蚀阈值测量及吸收特性分析, 强激光与粒子束, 21(2): 199-202.
引用本文: 张永强, 王贵兵, 唐小松, 王伟平. 2009: 两种纤维增强复合材料连续激光烧蚀阈值测量及吸收特性分析, 强激光与粒子束, 21(2): 199-202.
shu
Zhang Yongqiang, Wang Guibing, Tang Xiaosong, Wang Weiping. 2009: Ablation threshold measurement and absorption characteristic analysis of two fiber reinforced composites irradiated by CW laser, High Power Lase and Particle Beams, 21(2): 199-202.
Citation: Zhang Yongqiang, Wang Guibing, Tang Xiaosong, Wang Weiping. 2009: Ablation threshold measurement and absorption characteristic analysis of two fiber reinforced composites irradiated by CW laser, High Power Lase and Particle Beams, 21(2): 199-202.
shu

两种纤维增强复合材料连续激光烧蚀阈值测量及吸收特性分析

  • 中国工程物理研究院流体物理研究所,四川,绵阳,621900

Ablation threshold measurement and absorption characteristic analysis of two fiber reinforced composites irradiated by CW laser

  • 摘要: 通过双积分球-光电管测试系统和摄像记录的方法,对芳纶纤维/环氧和碳纤维/环氧两种复合材料在1.319 μm连续激光作用下的烧蚀阈值和烧蚀过程中材料对激光能量的吸收特性进行了实验研究.结果表明:芳纶纤维/环氧复合材料的平均烧蚀阈值随材料厚度增加而降低,碳纤维/环氧复合材料的平均烧蚀阈值不受材料厚度影响,约为70 W/cm2;两种纤维增强复合材料烧蚀前的反射率随激光功率增加而缓慢增大,芳纶纤维/环氧材料从0.40变化到0.45,碳纤维/环氧材料从0.15变化到0.20;当发生烧蚀时,芳纶纤维/环氧材料的反射率急剧下降,吸收率增大,碳纤维/环氧材料的反射率无明显变化,吸收率约为0.80.
  • 加载中
  • 加载中
计量
  • 文章访问数:  586
  • HTML全文浏览数:  147
  • PDF下载数:  72
  • 施引文献:  0
出版历程
  • 刊出日期:  2009-02-28

两种纤维增强复合材料连续激光烧蚀阈值测量及吸收特性分析

  • 中国工程物理研究院流体物理研究所,四川,绵阳,621900

摘要: 通过双积分球-光电管测试系统和摄像记录的方法,对芳纶纤维/环氧和碳纤维/环氧两种复合材料在1.319 μm连续激光作用下的烧蚀阈值和烧蚀过程中材料对激光能量的吸收特性进行了实验研究.结果表明:芳纶纤维/环氧复合材料的平均烧蚀阈值随材料厚度增加而降低,碳纤维/环氧复合材料的平均烧蚀阈值不受材料厚度影响,约为70 W/cm2;两种纤维增强复合材料烧蚀前的反射率随激光功率增加而缓慢增大,芳纶纤维/环氧材料从0.40变化到0.45,碳纤维/环氧材料从0.15变化到0.20;当发生烧蚀时,芳纶纤维/环氧材料的反射率急剧下降,吸收率增大,碳纤维/环氧材料的反射率无明显变化,吸收率约为0.80.