高级搜索

30.4nm Cr/Al/Cr自支撑滤光片的研制

,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

付联效, 吴永刚, 伍和云, 焦宏飞, 吕刚, 王振华. 2009: 30.4nm Cr/Al/Cr自支撑滤光片的研制, 强激光与粒子束, 21(2): 235-239.
引用本文: 付联效, 吴永刚, 伍和云, 焦宏飞, 吕刚, 王振华. 2009: 30.4nm Cr/Al/Cr自支撑滤光片的研制, 强激光与粒子束, 21(2): 235-239.
shu
Fu Lianxiao, Wu Yonggang, Wu Heyun, Jiao Hongfei, Lü Gang, Wang Zhenhua. 2009: Fabrication and characterization of 30.4 nm Cr/Al/Cr self-supporting filters, High Power Lase and Particle Beams, 21(2): 235-239.
Citation: Fu Lianxiao, Wu Yonggang, Wu Heyun, Jiao Hongfei, Lü Gang, Wang Zhenhua. 2009: Fabrication and characterization of 30.4 nm Cr/Al/Cr self-supporting filters, High Power Lase and Particle Beams, 21(2): 235-239.
shu

30.4nm Cr/Al/Cr自支撑滤光片的研制

  • 同济大学,精密光学工程技术研究所,上海,200092

Fabrication and characterization of 30.4 nm Cr/Al/Cr self-supporting filters

  • 摘要: 依据材料的质量吸收系数和波长的关系,选择Cr和Al设计和制备30.4 nm自支撑滤光片.在制备时以NaCl为脱膜剂,以热蒸发方式蒸镀Al,以电子束蒸发方式蒸镀Cr,制备了30.4 nm的Cr/Al/Cr自支撑滤光膜,并对滤光片的表面缺陷进行了分析.通过显微镜观察,滤光膜均匀纯净,无明显针孔.Cr/Al/Cr自支撑滤光片在合肥国家间步辐射实验室进行了测量,Cr/Al/Cr厚度为5 nm/500 nm/5 nm和12.5 nm/500nm/12.5 nm的滤光片在30.4 nm波长处的透过率分别为7.6%和4.6%,透过率曲线和理论计算基本一致.用紫外分光光度计测量得滤光片在200～800 nm波长范围的透过率小于0.02%,满足使用要求.
  • 加载中
  • 加载中
计量
  • 文章访问数:  375
  • HTML全文浏览数:  27
  • PDF下载数:  29
  • 施引文献:  0
出版历程
  • 刊出日期:  2009-02-28

30.4nm Cr/Al/Cr自支撑滤光片的研制

  • 同济大学,精密光学工程技术研究所,上海,200092

摘要: 依据材料的质量吸收系数和波长的关系,选择Cr和Al设计和制备30.4 nm自支撑滤光片.在制备时以NaCl为脱膜剂,以热蒸发方式蒸镀Al,以电子束蒸发方式蒸镀Cr,制备了30.4 nm的Cr/Al/Cr自支撑滤光膜,并对滤光片的表面缺陷进行了分析.通过显微镜观察,滤光膜均匀纯净,无明显针孔.Cr/Al/Cr自支撑滤光片在合肥国家间步辐射实验室进行了测量,Cr/Al/Cr厚度为5 nm/500 nm/5 nm和12.5 nm/500nm/12.5 nm的滤光片在30.4 nm波长处的透过率分别为7.6%和4.6%,透过率曲线和理论计算基本一致.用紫外分光光度计测量得滤光片在200～800 nm波长范围的透过率小于0.02%,满足使用要求.

English Abstract