高级搜索

40Cr钢表面激光熔覆层的磨损性能

,  ,  , 

downloadPDF

上一篇

下一篇

宋杰, 张庆茂, 林晓聪, 廖健宏. 2008: 40Cr钢表面激光熔覆层的磨损性能, 强激光与粒子束, 20(1): 21-25.
引用本文: 宋杰, 张庆茂, 林晓聪, 廖健宏. 2008: 40Cr钢表面激光熔覆层的磨损性能, 强激光与粒子束, 20(1): 21-25.
shu
SONG Jie, ZHANG Qing-mao, LIN Xiao-cong, LIAO Jian-hong. 2008: Wear performance of Fe-based alloy coating on the 40Cr steel treated by laser cladding, High Power Lase and Particle Beams, 20(1): 21-25.
Citation: SONG Jie, ZHANG Qing-mao, LIN Xiao-cong, LIAO Jian-hong. 2008: Wear performance of Fe-based alloy coating on the 40Cr steel treated by laser cladding, High Power Lase and Particle Beams, 20(1): 21-25.
shu

40Cr钢表面激光熔覆层的磨损性能

  • 华南师范大学,激光加工技术实验室,广州,510631

  • 广州瑞通千里激光设备有限公司,广州,510631

Wear performance of Fe-based alloy coating on the 40Cr steel treated by laser cladding

  • 摘要: 为研究模具钢熔覆层的磨损性能,采用铁基粉在40Cr钢表面进行激光熔覆,以激光熔覆层为上试样,GCr15钢珠为下试样,采用HT-500磨损试验机进行摩擦磨损试验,并与40Cr基体的磨损性能相对比.利用表面形貌仪测量磨痕深度和宽度.研究结果表明:载荷小于250 g时,相同载荷下基体的摩擦系数大.载荷小于300 g时,随磨损时间延长,熔覆层、基体的摩擦系数都随着载荷增加而减小.当载荷为300 g时,基体的摩擦系数在0.563～0.589之间变化,平均值为0.576,且随时间逐渐升高,耐磨性变差;熔覆层的磨擦系数在0.431～0.457之间变化,平均摩擦系数为0.444,磨痕深度和宽度分别是0.65 mm和1.096 μm,且随时间逐渐下降,表现了良好的耐磨性能.当载荷增加到500 g时,平均摩擦系数和磨痕深度比300 g时分别增加了75%和47倍,且摩擦系数逐渐升高,磨损性能下降.
  • 加载中
  • 加载中
计量
  • 文章访问数:  636
  • HTML全文浏览数:  118
  • PDF下载数:  131
  • 施引文献:  0
出版历程
  • 刊出日期:  2008-01-30

40Cr钢表面激光熔覆层的磨损性能

  • 华南师范大学,激光加工技术实验室,广州,510631
  • 广州瑞通千里激光设备有限公司,广州,510631

摘要: 为研究模具钢熔覆层的磨损性能,采用铁基粉在40Cr钢表面进行激光熔覆,以激光熔覆层为上试样,GCr15钢珠为下试样,采用HT-500磨损试验机进行摩擦磨损试验,并与40Cr基体的磨损性能相对比.利用表面形貌仪测量磨痕深度和宽度.研究结果表明:载荷小于250 g时,相同载荷下基体的摩擦系数大.载荷小于300 g时,随磨损时间延长,熔覆层、基体的摩擦系数都随着载荷增加而减小.当载荷为300 g时,基体的摩擦系数在0.563～0.589之间变化,平均值为0.576,且随时间逐渐升高,耐磨性变差;熔覆层的磨擦系数在0.431～0.457之间变化,平均摩擦系数为0.444,磨痕深度和宽度分别是0.65 mm和1.096 μm,且随时间逐渐下降,表现了良好的耐磨性能.当载荷增加到500 g时,平均摩擦系数和磨痕深度比300 g时分别增加了75%和47倍,且摩擦系数逐渐升高,磨损性能下降.