高级搜索

玻璃包覆铜丝快速凝固感应加热磁场数值模拟

,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

周秀文, 蔡红梅, 张继成, 刘德斌, 孙祚科, 余斌. 2007: 玻璃包覆铜丝快速凝固感应加热磁场数值模拟, 强激光与粒子束, 19(10): 1643-1648.
引用本文: 周秀文, 蔡红梅, 张继成, 刘德斌, 孙祚科, 余斌. 2007: 玻璃包覆铜丝快速凝固感应加热磁场数值模拟, 强激光与粒子束, 19(10): 1643-1648.
shu
ZHOU Xiu-wen, CAI Hong-mei, ZHANG Ji-cheng, LIU De-bin, SUN Zuo-ke, YU Bin. 2007: Magnetic field simulation of induction heating in glass-coated copper microwire rapid solidification process, High Power Lase and Particle Beams, 19(10): 1643-1648.
Citation: ZHOU Xiu-wen, CAI Hong-mei, ZHANG Ji-cheng, LIU De-bin, SUN Zuo-ke, YU Bin. 2007: Magnetic field simulation of induction heating in glass-coated copper microwire rapid solidification process, High Power Lase and Particle Beams, 19(10): 1643-1648.
shu

玻璃包覆铜丝快速凝固感应加热磁场数值模拟

  • 中国工程物理研究院,激光聚变研究中心,四川,绵阳,621900

Magnetic field simulation of induction heating in glass-coated copper microwire rapid solidification process

  • 摘要: 建立了玻璃包覆铜丝快速凝固感应加热电磁场计算模型,借助MATLAB软件描述了圆柱形导体内电磁场分布规律.研究了感应线圈直径、锥度和匝数等参数对感应线圈内磁场分布的影响.结果表明: 随着感应线圈直径的增大,最大磁场强度降低;随着锥度的增大,线圈中最大磁场强度降低;随着感应线圈匝数增加,线圈中的最大磁场强度增加.扫描电镜和X射线衍射仪分析表明,实验制备的玻璃包覆铜丝的直径为18 μm、铜丝的直径为3.3 μm,玻璃包覆铜丝的表面质量及直径均匀性较好,铜以晶态形式存在,在[200]晶向具有明显的择优取向.
  • 加载中
  • 加载中
计量
  • 文章访问数:  459
  • HTML全文浏览数:  23
  • PDF下载数:  60
  • 施引文献:  0
出版历程
  • 刊出日期:  2007-10-30

玻璃包覆铜丝快速凝固感应加热磁场数值模拟

  • 中国工程物理研究院,激光聚变研究中心,四川,绵阳,621900

摘要: 建立了玻璃包覆铜丝快速凝固感应加热电磁场计算模型,借助MATLAB软件描述了圆柱形导体内电磁场分布规律.研究了感应线圈直径、锥度和匝数等参数对感应线圈内磁场分布的影响.结果表明: 随着感应线圈直径的增大,最大磁场强度降低;随着锥度的增大,线圈中最大磁场强度降低;随着感应线圈匝数增加,线圈中的最大磁场强度增加.扫描电镜和X射线衍射仪分析表明,实验制备的玻璃包覆铜丝的直径为18 μm、铜丝的直径为3.3 μm,玻璃包覆铜丝的表面质量及直径均匀性较好,铜以晶态形式存在,在[200]晶向具有明显的择优取向.