高级搜索

分层蒸镀制备聚酰亚胺自支撑膜及其特性研究

,  ,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

戚同非, 吴永刚, 王勇, 张莉, 林小燕, 田国勋, 焦宏飞, 陈玲燕. 2005: 分层蒸镀制备聚酰亚胺自支撑膜及其特性研究, 强激光与粒子束, 17(10): 1528-1532.
引用本文: 戚同非, 吴永刚, 王勇, 张莉, 林小燕, 田国勋, 焦宏飞, 陈玲燕. 2005: 分层蒸镀制备聚酰亚胺自支撑膜及其特性研究, 强激光与粒子束, 17(10): 1528-1532.
shu
QI Tong-fei, WU Yong-gang, WANG Yong, ZHANG Li, LIN Xiao-yan, TIAN Guo-xun, JIAO Hong-fei, CHEN Ling-yan. 2005: Preparation of ultra-thin freestanding polyimide films with sequential evaporation technique, High Power Lase and Particle Beams, 17(10): 1528-1532.
Citation: QI Tong-fei, WU Yong-gang, WANG Yong, ZHANG Li, LIN Xiao-yan, TIAN Guo-xun, JIAO Hong-fei, CHEN Ling-yan. 2005: Preparation of ultra-thin freestanding polyimide films with sequential evaporation technique, High Power Lase and Particle Beams, 17(10): 1528-1532.
shu

分层蒸镀制备聚酰亚胺自支撑膜及其特性研究

  • 同济大学,波耳固体物理研究所,精密光学工程技术研究所,上海,200092

Preparation of ultra-thin freestanding polyimide films with sequential evaporation technique

  • 摘要: 采用分层蒸镀法,在玻璃基片上依次蒸镀二氨基二苯醚(ODA)和均苯四甲酸二酐(PMDA)两种单体,然后在空气环境中对样品进行不同温度和时间的热亚胺化处理,使二者在交界面上反应生成聚酰亚胺.经加热150 ℃ 1 h然后经350 ℃ 2 h处理的样品,在脱膜后能制备出直径1.8 cm,厚度为100 nm的聚酰亚胺自支撑薄膜.用FTIR测量了自支撑薄膜的红外光谱,特征吸收峰的分析表明薄膜已基本上完全亚胺化.用原子力显微镜分析了浮法玻璃衬底上聚酰亚胺薄膜的表面形貌,结果表明以ODA作为内层制备的膜层表面更光滑平整.
  • 加载中
  • 加载中
计量
  • 文章访问数:  360
  • HTML全文浏览数:  31
  • PDF下载数:  31
  • 施引文献:  0
出版历程
  • 刊出日期:  2005-10-30

分层蒸镀制备聚酰亚胺自支撑膜及其特性研究

  • 同济大学,波耳固体物理研究所,精密光学工程技术研究所,上海,200092

摘要: 采用分层蒸镀法,在玻璃基片上依次蒸镀二氨基二苯醚(ODA)和均苯四甲酸二酐(PMDA)两种单体,然后在空气环境中对样品进行不同温度和时间的热亚胺化处理,使二者在交界面上反应生成聚酰亚胺.经加热150 ℃ 1 h然后经350 ℃ 2 h处理的样品,在脱膜后能制备出直径1.8 cm,厚度为100 nm的聚酰亚胺自支撑薄膜.用FTIR测量了自支撑薄膜的红外光谱,特征吸收峰的分析表明薄膜已基本上完全亚胺化.用原子力显微镜分析了浮法玻璃衬底上聚酰亚胺薄膜的表面形貌,结果表明以ODA作为内层制备的膜层表面更光滑平整.