高级搜索

双掺杂的Sm0.9Sr0.1Al1-xCoxO3-δ钙钛矿结构导电陶瓷的制备及其电性能

,  ,  , 

downloadPDF

上一篇

下一篇

向军, 郭银涛, 褚艳秋, 周广振. 2011: 双掺杂的Sm0.9Sr0.1Al1-xCoxO3-δ钙钛矿结构导电陶瓷的制备及其电性能, 物理学报, 60(2): 602-607.
引用本文: 向军, 郭银涛, 褚艳秋, 周广振. 2011: 双掺杂的Sm0.9Sr0.1Al1-xCoxO3-δ钙钛矿结构导电陶瓷的制备及其电性能, 物理学报, 60(2): 602-607.
shu
Xiang Jun, Guo Yin-Tao, Chu Yan-Qiu, Zhou Guang-Zhen. 2011: Preparation and electrical properties of double-doped perovskite structured conducting ceramics Sm0.9Sr0.1Al1-xCox O3-δ, Acta Physica Sinica, 60(2): 602-607.
Citation: Xiang Jun, Guo Yin-Tao, Chu Yan-Qiu, Zhou Guang-Zhen. 2011: Preparation and electrical properties of double-doped perovskite structured conducting ceramics Sm0.9Sr0.1Al1-xCox O3-δ, Acta Physica Sinica, 60(2): 602-607.
shu

双掺杂的Sm0.9Sr0.1Al1-xCoxO3-δ钙钛矿结构导电陶瓷的制备及其电性能

  • 江苏科技大学数理学院,镇江,212003

Preparation and electrical properties of double-doped perovskite structured conducting ceramics Sm0.9Sr0.1Al1-xCox O3-δ

  • 摘要: 采用有机凝胶法结合高温烧结制备了Sm0.9Sr0.1Al1-xCoxO3-δ(SSAC,x=0.2,0.4,0.5,0.6)系列钙钛矿结构混合导电陶瓷,并详细讨论了烧结温度和Co掺杂量对其晶体结构、相组成和电性能的影响.X射线衍射结果显示,过高的烧结温度或Co掺杂量都会导致杂相Sm(Sr)CoO3生成,Co在该体系的固溶限位于50 mol%-60 mol%之间,Co对Al的部分取代使晶格体积增大.电性能测量结果表明,SSAC陶瓷的电导率主要取决于p型电导,其导电行为符合小极化子跳跃导电机制;随着烧结温度的升高,材料的电导率逐渐增大;在固溶限内随Co含量的增加,SSAC陶瓷的电导率增大,表观活化能减小;1200 ℃烧结10 h制得的单相Sm0.9Sr0.1Al0.5Co0.5O3-δ陶瓷体在800 ℃的电导率达63.4 S/cm,表观活化能为0.14 eV.具有良好电性能的SSAC导电陶瓷有望应用于高温电化学领域.
  • 加载中
  • 加载中
计量
  • 文章访问数:  517
  • HTML全文浏览数:  109
  • PDF下载数:  0
  • 施引文献:  0
出版历程
  • 刊出日期:  2011-02-28

双掺杂的Sm0.9Sr0.1Al1-xCoxO3-δ钙钛矿结构导电陶瓷的制备及其电性能

  • 江苏科技大学数理学院,镇江,212003

摘要: 采用有机凝胶法结合高温烧结制备了Sm0.9Sr0.1Al1-xCoxO3-δ(SSAC,x=0.2,0.4,0.5,0.6)系列钙钛矿结构混合导电陶瓷,并详细讨论了烧结温度和Co掺杂量对其晶体结构、相组成和电性能的影响.X射线衍射结果显示,过高的烧结温度或Co掺杂量都会导致杂相Sm(Sr)CoO3生成,Co在该体系的固溶限位于50 mol%-60 mol%之间,Co对Al的部分取代使晶格体积增大.电性能测量结果表明,SSAC陶瓷的电导率主要取决于p型电导,其导电行为符合小极化子跳跃导电机制;随着烧结温度的升高,材料的电导率逐渐增大;在固溶限内随Co含量的增加,SSAC陶瓷的电导率增大,表观活化能减小;1200 ℃烧结10 h制得的单相Sm0.9Sr0.1Al0.5Co0.5O3-δ陶瓷体在800 ℃的电导率达63.4 S/cm,表观活化能为0.14 eV.具有良好电性能的SSAC导电陶瓷有望应用于高温电化学领域.