高级搜索

(Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应

,  ,  , 

downloadPDF

上一篇

下一篇

张茹, 王淼, 张宁, Srinivasan G. 2006: (Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应, 物理学报, 55(5): 2548-2552. doi: 10.3321/j.issn:1000-3290.2006.05.074
引用本文: 张茹, 王淼, 张宁, Srinivasan G. 2006: (Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应, 物理学报, 55(5): 2548-2552. doi: 10.3321/j.issn:1000-3290.2006.05.074
shu
Zhang Ru, Wang Miao, Zhang Ning, Srinivasan G. 2006: Magnetoelectric effect in bilayers of (Ni0.8Zn0.2Fe2O4)epoxy-PZT, Acta Physica Sinica, 55(5): 2548-2552. doi: 10.3321/j.issn:1000-3290.2006.05.074
Citation: Zhang Ru, Wang Miao, Zhang Ning, Srinivasan G. 2006: Magnetoelectric effect in bilayers of (Ni0.8Zn0.2Fe2O4)epoxy-PZT, Acta Physica Sinica, 55(5): 2548-2552. doi: 10.3321/j.issn:1000-3290.2006.05.074
shu

(Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应

  • 南京师范大学磁电子学实验室,南京,210097

  • 南京师范大学磁电子学实验室,南京,210097;奥克兰大学物理系,罗切斯特,MI48309,USA

Magnetoelectric effect in bilayers of (Ni0.8Zn0.2Fe2O4)epoxy-PZT

  • 摘要: 讨论了Ni0.8Zn0.2Fe2O4(NZFO)与锆钛酸铅(PZT)的双层膜结构样品的磁电(ME)效应.NZFO粉料由溶胶-凝胶法制成,再经900℃热压,并高温烧结.在该双层膜中测量到了很强的磁电相互作用.发现横向的磁电效应比纵向效应大一个数量级,并且随NZFO烧结温度的提高而增加.当烧结温度从950℃上升到1380℃时,横向ME电压系数(αE)的最大值变化范围为25.6 mV Am-2≤αE≤199.6 mV Am-2.理论分析显示NZFO-PZT双层膜样品中ME效应源于NZFO与PZT之间相对良好的磁电耦合.
  • 加载中
  • 加载中
计量
  • 文章访问数:  548
  • HTML全文浏览数:  92
  • PDF下载数:  41
  • 施引文献:  0
出版历程
  • 刊出日期:  2006-05-30

(Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应

  • 南京师范大学磁电子学实验室,南京,210097
  • 南京师范大学磁电子学实验室,南京,210097;奥克兰大学物理系,罗切斯特,MI48309,USA

摘要: 讨论了Ni0.8Zn0.2Fe2O4(NZFO)与锆钛酸铅(PZT)的双层膜结构样品的磁电(ME)效应.NZFO粉料由溶胶-凝胶法制成,再经900℃热压,并高温烧结.在该双层膜中测量到了很强的磁电相互作用.发现横向的磁电效应比纵向效应大一个数量级,并且随NZFO烧结温度的提高而增加.当烧结温度从950℃上升到1380℃时,横向ME电压系数(αE)的最大值变化范围为25.6 mV Am-2≤αE≤199.6 mV Am-2.理论分析显示NZFO-PZT双层膜样品中ME效应源于NZFO与PZT之间相对良好的磁电耦合.