高级搜索

Dy掺杂对Sr2Bi4Ti5O18铁电陶瓷性能的影响

,  ,  , 

downloadPDF

上一篇

下一篇

羌锋, 朱骏, 毛翔宇, 陈小兵. 2005: Dy掺杂对Sr2Bi4Ti5O18铁电陶瓷性能的影响, 物理学报, 54(11): 5422-5427. doi: 10.3321/j.issn:1000-3290.2005.11.076
引用本文: 羌锋, 朱骏, 毛翔宇, 陈小兵. 2005: Dy掺杂对Sr2Bi4Ti5O18铁电陶瓷性能的影响, 物理学报, 54(11): 5422-5427. doi: 10.3321/j.issn:1000-3290.2005.11.076
shu
Qiang Feng, Zhu Jun, Mao Xiang-Yu, Chen Xiao-Bing. 2005: Effect of Dy-doping on the properties of Sr2Bi4Ti5O18 ferroelectric ceramics, Acta Physica Sinica, 54(11): 5422-5427. doi: 10.3321/j.issn:1000-3290.2005.11.076
Citation: Qiang Feng, Zhu Jun, Mao Xiang-Yu, Chen Xiao-Bing. 2005: Effect of Dy-doping on the properties of Sr2Bi4Ti5O18 ferroelectric ceramics, Acta Physica Sinica, 54(11): 5422-5427. doi: 10.3321/j.issn:1000-3290.2005.11.076
shu

Dy掺杂对Sr2Bi4Ti5O18铁电陶瓷性能的影响

  • 扬州大学物理科学与技术学院,扬州,225002

Effect of Dy-doping on the properties of Sr2Bi4Ti5O18 ferroelectric ceramics

  • 摘要: 用传统固相烧结法制备了Sr2Bi4-xDyxTi5O18(SBDT-x,x=0-0.20)陶瓷样品.x射线衍射分析表明,微量的Dy掺杂没有影响Sr2Bi4Ti5O18(SBTi)原有的层状钙钛矿结构.通过研究样品的介电特性,发现Dy掺杂减小了材料的损耗因子,降低了样品铁电-顺电相转变的居里温度.铁电性能测量结果表明,随Dy含量的增加,SBDT-x系列样品的剩余极化先增大,后减小.当Dy掺杂量为O.01时,剩余极化达到最大值,约为20.1 μC·cm-2.掺杂引起剩余极化的变化,与材料中缺陷浓度、内应力以及晶格畸变程度等因素有关,是多种作用机理相互竞争的结果.(Bi2O2)2+层通常被看作是绝缘层和空间电荷库,对材料的铁电性能起关键作用.掺杂离子进入(Bi2O2)2+层会导致铁电性能变差.
  • 加载中
  • 加载中
计量
  • 文章访问数:  362
  • HTML全文浏览数:  49
  • PDF下载数:  9
  • 施引文献:  0
出版历程
  • 刊出日期:  2005-11-30

Dy掺杂对Sr2Bi4Ti5O18铁电陶瓷性能的影响

  • 扬州大学物理科学与技术学院,扬州,225002

摘要: 用传统固相烧结法制备了Sr2Bi4-xDyxTi5O18(SBDT-x,x=0-0.20)陶瓷样品.x射线衍射分析表明,微量的Dy掺杂没有影响Sr2Bi4Ti5O18(SBTi)原有的层状钙钛矿结构.通过研究样品的介电特性,发现Dy掺杂减小了材料的损耗因子,降低了样品铁电-顺电相转变的居里温度.铁电性能测量结果表明,随Dy含量的增加,SBDT-x系列样品的剩余极化先增大,后减小.当Dy掺杂量为O.01时,剩余极化达到最大值,约为20.1 μC·cm-2.掺杂引起剩余极化的变化,与材料中缺陷浓度、内应力以及晶格畸变程度等因素有关,是多种作用机理相互竞争的结果.(Bi2O2)2+层通常被看作是绝缘层和空间电荷库,对材料的铁电性能起关键作用.掺杂离子进入(Bi2O2)2+层会导致铁电性能变差.

English Abstract