高级搜索

355nm纳秒紫外激光辐照下熔石英前后表面损伤的对比研究

,  ,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

刘红婕, 周信达, 黄进, 王凤蕊, 蒋晓东, 黄竞, 吴卫东, 郑万国. 2011: 355nm纳秒紫外激光辐照下熔石英前后表面损伤的对比研究, 物理学报, 60(6): 453-458.
引用本文: 刘红婕, 周信达, 黄进, 王凤蕊, 蒋晓东, 黄竞, 吴卫东, 郑万国. 2011: 355nm纳秒紫外激光辐照下熔石英前后表面损伤的对比研究, 物理学报, 60(6): 453-458.
shu
Liu Hong-Jie, Zhou Xin-Da, Huang Jin, Wang Feng-Rui, Jiang Xiao-Dong, Huang Jing, Wu Wei-Dong, Zheng Wan-Guo. 2011: Comparison of damage between front and rear surfaces under nanosecond 355nm laser irradiation on fused silica, Acta Physica Sinica, 60(6): 453-458.
Citation: Liu Hong-Jie, Zhou Xin-Da, Huang Jin, Wang Feng-Rui, Jiang Xiao-Dong, Huang Jing, Wu Wei-Dong, Zheng Wan-Guo. 2011: Comparison of damage between front and rear surfaces under nanosecond 355nm laser irradiation on fused silica, Acta Physica Sinica, 60(6): 453-458.
shu

355nm纳秒紫外激光辐照下熔石英前后表面损伤的对比研究

  • 中国工程物理研究院激光聚变研究中心,绵阳,621900

Comparison of damage between front and rear surfaces under nanosecond 355nm laser irradiation on fused silica

  • 摘要: 为了理解前后表面损伤不对称性的物理内涵,利用阴影成像技术研究了纳秒紫外激光诱使熔石英光学元件表面损伤的时间分辨动力学过程.研究表明,纳秒紫外激光与熔石英作用过程中前后表面损伤的物理机理是完全不同的.前表面处空气中等离子体和冲击波较强,等离子体的屏蔽作用抑制了余脉冲能量的沉积,降低了元件损伤程度.而后表面处等离子体吸收激光能量膨胀,对后表面冲击作用更为严重,形成的等离子体电子密度可达到1023cm-3以上,反射部分激光能量与入射的激光余脉冲干涉,使得损伤更为严重.研究结果对理解损伤的机理有重要意义.
  • 加载中
  • 加载中
计量
  • 文章访问数:  546
  • HTML全文浏览数:  211
  • PDF下载数:  0
  • 施引文献:  0
出版历程

355nm纳秒紫外激光辐照下熔石英前后表面损伤的对比研究

  • 中国工程物理研究院激光聚变研究中心,绵阳,621900

摘要: 为了理解前后表面损伤不对称性的物理内涵,利用阴影成像技术研究了纳秒紫外激光诱使熔石英光学元件表面损伤的时间分辨动力学过程.研究表明,纳秒紫外激光与熔石英作用过程中前后表面损伤的物理机理是完全不同的.前表面处空气中等离子体和冲击波较强,等离子体的屏蔽作用抑制了余脉冲能量的沉积,降低了元件损伤程度.而后表面处等离子体吸收激光能量膨胀,对后表面冲击作用更为严重,形成的等离子体电子密度可达到1023cm-3以上,反射部分激光能量与入射的激光余脉冲干涉,使得损伤更为严重.研究结果对理解损伤的机理有重要意义.

English Abstract