高级搜索

玻璃微球壁厚和预充气工艺对气体渗透性能的影响

,  ,  ,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

张占文, 李波, 唐永建, 王朝阳, 漆小波, 陈素芬, 刘一杨, 翟世明. 2006: 玻璃微球壁厚和预充气工艺对气体渗透性能的影响, 强激光与粒子束, 18(6): 957-960.
引用本文: 张占文, 李波, 唐永建, 王朝阳, 漆小波, 陈素芬, 刘一杨, 翟世明. 2006: 玻璃微球壁厚和预充气工艺对气体渗透性能的影响, 强激光与粒子束, 18(6): 957-960.
shu
ZHANG Zhan-wen, LI Bo, TANG Yong-jian, WANG Chao-yang, QI Xiao-bo, CHEN Su-fen, LIU Yi-yang, ZHAI Shi-ming. 2006: Influence of wall thickness and filling gas procedure on permeability of hollow glass microsphere, High Power Lase and Particle Beams, 18(6): 957-960.
Citation: ZHANG Zhan-wen, LI Bo, TANG Yong-jian, WANG Chao-yang, QI Xiao-bo, CHEN Su-fen, LIU Yi-yang, ZHAI Shi-ming. 2006: Influence of wall thickness and filling gas procedure on permeability of hollow glass microsphere, High Power Lase and Particle Beams, 18(6): 957-960.
shu

玻璃微球壁厚和预充气工艺对气体渗透性能的影响

  • 中国工程物理研究院,激光聚变研究中心,四川,绵阳,621900

Influence of wall thickness and filling gas procedure on permeability of hollow glass microsphere

  • 摘要: 以空心玻璃微球为研究对象,利用高压充气系统充气,测量了不同条件下玻璃微球对氘气在室温条件下的气体渗透系数.研究结果表明:微球的壁厚对气体渗透系数影响较大,2 μm以上厚壁球的气体渗透系数约5.0×10-22 mol·m-1·s-1·Pa-1,而壁厚小于1 μm时,渗透系数约1.56×10-20 mol·m-1·s-1·Pa-1,两者相差30倍.预充气挑选工艺对微球的气体渗透系数也产生一定影响,对于薄壁空心玻璃微球一次充放气气体渗透系数增加约50%,两次充放气则增大一倍左右.对上述影响因素进行了初步的探讨,气体渗透系数改变的主要原因是玻璃微球表面的结构裂纹、空位和缺陷.
  • 加载中
  • 加载中
计量
  • 文章访问数:  412
  • HTML全文浏览数:  41
  • PDF下载数:  29
  • 施引文献:  0
出版历程
  • 刊出日期:  2006-06-30

玻璃微球壁厚和预充气工艺对气体渗透性能的影响

  • 中国工程物理研究院,激光聚变研究中心,四川,绵阳,621900

摘要: 以空心玻璃微球为研究对象,利用高压充气系统充气,测量了不同条件下玻璃微球对氘气在室温条件下的气体渗透系数.研究结果表明:微球的壁厚对气体渗透系数影响较大,2 μm以上厚壁球的气体渗透系数约5.0×10-22 mol·m-1·s-1·Pa-1,而壁厚小于1 μm时,渗透系数约1.56×10-20 mol·m-1·s-1·Pa-1,两者相差30倍.预充气挑选工艺对微球的气体渗透系数也产生一定影响,对于薄壁空心玻璃微球一次充放气气体渗透系数增加约50%,两次充放气则增大一倍左右.对上述影响因素进行了初步的探讨,气体渗透系数改变的主要原因是玻璃微球表面的结构裂纹、空位和缺陷.