高级搜索

La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04)异质pn结的整流特性

,  ,  ,  , 

downloadPDF

上一篇

下一篇

李彤, 李驰平, 张铭, 王波, 严辉. 2007: La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04)异质pn结的整流特性, 物理学报, 56(7): 4132-4136. doi: 10.3321/j.issn:1000-3290.2007.07.082
引用本文: 李彤, 李驰平, 张铭, 王波, 严辉. 2007: La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04)异质pn结的整流特性, 物理学报, 56(7): 4132-4136. doi: 10.3321/j.issn:1000-3290.2007.07.082
shu
Li Tong, Li Chi-Ping, Zhang Ming, Wang Bo, Yan Hui. 2007: Rectifying characteristics of La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04) pn heterojunctions, Acta Physica Sinica, 56(7): 4132-4136. doi: 10.3321/j.issn:1000-3290.2007.07.082
Citation: Li Tong, Li Chi-Ping, Zhang Ming, Wang Bo, Yan Hui. 2007: Rectifying characteristics of La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04) pn heterojunctions, Acta Physica Sinica, 56(7): 4132-4136. doi: 10.3321/j.issn:1000-3290.2007.07.082
shu

La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04)异质pn结的整流特性

  • 北京工业大学材料科学与工程学院,北京,100022

Rectifying characteristics of La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04) pn heterojunctions

  • 摘要: 采用磁控溅射法制备的La1-xSrxMnO3(LSMO)/TiO2异质pn结表现出很好的整流特性.室温电流电压特性曲线显示随着Sr掺杂的增加,扩散电压增大,这可能由于Sr掺杂的增加导致载流子浓度增大所致.电流电压变温特性曲线显示随着测量温度的降低,扩散电压增大,这可能由于随着测量温度的变化导致界面电子结构的变化所致.值得提出的,异质pn结电阻随温度变化曲线表现出单层LSMO的金属绝缘相变特性,并且在低测量温度时表现出随着测量温度的降低结电阻增大,这可能是由于宽带隙的TiO2的引入导致.
  • 加载中
  • 加载中
计量
  • 文章访问数:  395
  • HTML全文浏览数:  61
  • PDF下载数:  21
  • 施引文献:  0
出版历程
  • 刊出日期:  2007-07-30

La1-xSrxMnO3/TiO2(x=0.2,0.15,0.04)异质pn结的整流特性

  • 北京工业大学材料科学与工程学院,北京,100022

摘要: 采用磁控溅射法制备的La1-xSrxMnO3(LSMO)/TiO2异质pn结表现出很好的整流特性.室温电流电压特性曲线显示随着Sr掺杂的增加,扩散电压增大,这可能由于Sr掺杂的增加导致载流子浓度增大所致.电流电压变温特性曲线显示随着测量温度的降低,扩散电压增大,这可能由于随着测量温度的变化导致界面电子结构的变化所致.值得提出的,异质pn结电阻随温度变化曲线表现出单层LSMO的金属绝缘相变特性,并且在低测量温度时表现出随着测量温度的降低结电阻增大,这可能是由于宽带隙的TiO2的引入导致.

English Abstract